Abstract:Abstract The coastal pipelines are the key link between the offshore and the onshore pipelines, which are located in the soil dry-wet alternating environment. Even though higher corrosion risk of metals in coastal soil dry-wet alternating environment, few papers focused on this condition, while much research about ocean and atmospheric dry-wet alternating environment was paid attention to. In this paper, a self-designed soil dry-wet alternating experimental device was used to investigate the corrosion characteristics of Q235 steel in seawater, soil and dry-wet alternating environment based on mass loss experiments, corrosion morphology analysis and electrochemical experiments. The results showed that the general corrosion rate of Q235 steel in soil and seawater environments basically remained unchanged, and in dry-wet alternating environment increased with time, while the pitting rates were 0.280 mm/a (soil), 0.420 mm/a (seawater) and 0.567 mm/a (dry-wet alternation), respectively, which was caused by the oxygen concentration cell and salt concentration cell. Meanwhile, the growth rate of pitting size in dry-wet alternating environment was much higher than that in the other two environments with different corrosion characteristics of pitting corrosion (seawater and dry-wet alternation) and a changed from general corrosion to pitting corrosion (soil). In three environments, the corrosion current density ( I corr ) increased, in which on the 30th day of experiment, I corr = 79.72 μ A cm −2 in dry-wet alternating environment, which was much higher than I corr = 47.89 μ A cm −2 in seawater environment. In dry-wet alternating environment, the mass diffusion impedance at 10 –2 Hz and the maximum phase angle changed significantly, while the log f -log∣ Z ∣ curve in low-middle frequency decreased significantly, and charge transfer resistance at 10 5 Hz reduced from 10.4 Ω to 4.3 Ω, illustrating an increasing corrosion rate.

Corrosion Behavior of Q235B Steel and L245 Steel in Dalian Soil Saturated with Water

Corrosion Behaviors and Mechanical Properties of Q235 Steel Pipes Collapsing Due to Corrosion after 25-Year Service in Urban Industrial Atmospheric Environment

Influence of Sulfide Ion in Accumulated Water in Coal Gas Pipeline on Q235B Steel Corrosion

Research on the Corrosion Behavior of Q235 Pipeline Steel in an Atmospheric Environment through Experiment

Study on corrosion characteristics of Q235 steel in seawater, soil and dry-wet alternating environments focusing on Shengli oilfield

Investigation of Q235 steel electrochemical corrosion behavior in naturally dried sandy soil

Study on the corrosion behavior of L245 pipeline steel in 100LL aviation gasoline wastewater

Influence of Cl- and SO2 on Carbon Steel Q235, Pipeline Steel L415 and Pressure Vessel Steel 16MnNi Corrosion Behavior in Industrial and Marine Atmosphere Environment

Corrosion Behavior of X80 Pipeline Steel in Alkaline Sand Soil with Saturated Water

The Corrosion Features of Q235B Steel under Immersion Test and Electrochemical Measurements in Desulfurization Solution.

A comparative study on the corrosion behavior of Q235 steel in saturated acidic red and yellow soils

Corrosion Behavior of 35crmn and Q235 Steel in Simulated Acid Rain Conditions

Experimental study on Q235 steel in soil polluted by NaCl after corrosion

Corrosion Behavior of the Steel Used As a Huge Storage Tank in Seawater

Corrosion Behavior of Carbon Steel Pipelines under Different Deposits in Oil and Gas Transportation

Influence of Cathode Protection on Corrosion Resistance of Q235 Steel in Lanzhou Soil

Corrosion Behavior of API Spec X60 Pipeline Steels in Seamud

Study on Electrochemical Corrosion Behavior of X80 Pipeline Steel in Luoyang Soil with Saturated Water

Electrochemical corrosion behaviour of four low-carbon steels in saline soil

Corrosion behaviors of arc spraying single and double layer coatings in simulated Dagang soil solution

Corrosion behavior of Q235 steel with polysiloxane composite coating in different environment