Performance of Oxidation Resistant Coatings for C/C Composites As Aircraft Brakes

Xiao Zhi-chao,Xue Ning-juan,Su Jun-min,Peng Zhi-gang,Jin Zhi-hao,Hao Zhi-biao

DOI: https://doi.org/10.1016/j.carbon.2010.03.060

IF: 10.9

2010-01-01

Carbon

Abstract:A modified phosphate coating on C/C composites used for aircraft brakes was made from zinc chloride, phosphoric acid, zinc phosphate and aluminum phosphate. In order to study the properties of the modified coating, an unmodified phosphate coating and a ceramic coating, which principally consists of silicon and boron, were also investigated. Results showed that all three coatings had excellent oxidation resistance at 500 degrees C for 100 h and the maximum mass loss is 1.25%. The mass loss of the C/C composite with a modified phosphate coating was 1.76% when the composite was subjected to oxidation at 700 degrees C for 30 h in air, and the value was 1. 98% when the composite was subjected to thermal shock in air for 30 cycles (from 900 degrees C for 3 min to at room temperature for 2 min) followed by shock in air for 10 cycles (from 1100 degrees C for 3 min to room temperature for 2 min). The performance of the modified phosphate coating is the best among the three coatings. It has excellent oxidation resistance and thermal shock resistance.