Texture Development and Superconducting Properties of YBCO Thick Films Deposited on Buffered Metal Substrates at Various Deposition Rates

YJ Li,K Zdun,L Hope,J Xie,S Corcoran,Y Qiao,J Reeves,K Lenseth,V Selvamanickam

DOI: https://doi.org/10.1109/tasc.2003.811997

IF: 1.9489

2003-01-01

IEEE Transactions on Applied Superconductivity

Abstract:YBa2Cu3O7-x, (YBCO) thick films have been grown on buffered metal substrates at different deposition rates by pulsed laser deposition (PLD). In-plane texture and supeconducting properties of YBCO films have been systematically investigated: It was observed that the in-situ epitaxial growth of YBCO films on buffered metal substrates could be achieved at a very high deposition rate. Under the optimized deposition conditions; X-ray diffraction measurements showed that both in-plane and out-plane texture of YBCO films were mainly dependent on the texture quality of the buffer-layer not the deposition rate. As the deposition rate increased from 1 nm/s to 30 nm/s, the average phi-scan rocking curve of YBCO films was only increased from 10 degree to 12 degree. The omega scan rocking curves kept the same FWHM value of 2 degree. Critical current densities J(c) of the order of 10(6) A/cm(2) at 77 K and self-field have been achieved at high deposition rate of 30 nm/s by optimizing deposition parameters. Our results demonstrate the practical possibility of YBCO thick film processing at very high deposition rate by PLD on buffered metal substrates.