Microstructures and Electric Characteristics of SrNdCoO4 Ceramics with K2NiF4 Structure

Y. Y. Liu,X. M. Chen,X. Q. Liu,L. Li
DOI: https://doi.org/10.1007/s10832-007-9261-9
2007-01-01
Journal of Electroceramics
Abstract:SrNdCoO4 ceramics with tetragonal K2NiF4 structure were prepared by a solid-state reaction process. The frequency and temperature dependence of dielectric and conductive properties were studied. A peak was found at similar to 325 degrees C on both dielectric constant (epsilon) and conductivity (sigma) plots with temperature. After annealing in O-2, the peak of epsilon disappeared while that of sigma just shifted a little toward high temperature side. So, some oxide vacancies existed in the polycrystalline SrNdCoO4, which contributed much to epsilon but influenced sigma only slightly in the measured temperature and frequency range. A lower resistivity of 3.7 Omega cm was obtained in SrNdCoO4 ceramics sintered at 1150 degrees C.