Abstract:In this study, a novel sol-gel method is used to synthesize amorphous silica-alumina materials with a narrow mesoporous distribution and various Si/Al molar ratios without using any templates and pore-regulating agents. During the preparation procedure, only inexpensive inorganic salts were used as raw materials, instead of expensive and harmful alkoxides. The precursor sol was dried at room temperature in a vacuum box kept at 60 mmHg until it began to form the gel. The results of a nitrogen sorption experiment indicate that the synthesized materials with different Si/Al molar ratios have similar mesoporous distributions (within 2-12 nm). Moreover, it was found that the material's pore size distribution remains at a similar value during the heat treatment from room temperature to 550 degreesC. On the basis of the nitrogen sorption, TEM, and AFM characterization results, a formation mechanism of mesopores which accounts for the experimental data is also suggested. This suggested mechanism involves rearrangement of the primary particles during the drying process to form the precursors of the similarly sized mesopores. The synthesized materials were characterized by XRD, thermal analysis (TG/DTA), Al-27 and Si-29 MAS NMR spectroscopy, SEM, TEM, and AFM. The results of Al-27 and 29Si MAS NMR indicate that the distribution of silicon and aluminum in the synthesized materials is more uniform and homogeneous than that in the mixed oxides prepared via the traditional sol-gel method even at high alumina contents. The type and density of the acid sites were studied using pyridine adsorption-desorption FTIR spectroscopy. It was shown that the acidity of the synthesized materials is higher than that of the silica-alumina materials prepared by conventional methods.

Synthesizing Silicon Nitride Whiskers by Solvothermal and Carbothermal Methods

Sol–gel preparation of Ge nanocrystals embedded in SiO2 glasses

Synthesizing nano-scale titanium nitride powders by solvothermal and carbothermal methods

A New Synthesis Method for Producing Si3n4 Whiskers by Heat Treating Porous Si Objects

Synthesis of SiCN Xerogel and Ceramics by a Non-Oxide Sol-Gel Process

Synthesis and Characterization of Nanostructured Silicon Carbide Crystal Whiskers by Sol–gel Process and Carbothermal Reduction

Non-catalytic Vapor Synthesis of Α-Si3n4 Nanowhiskers Via Direct Nitridation of Silicon Powders

Synthesis of alpha-Si3N4 whiskers or equiaxed particles from amorphous Si3N4 powders

A New Route to Synthesize SiC−AlN Solid Solution Whiskers

In situ synthesis of high-purity α-Si3N4 whiskers from amorphous Si-N-C powders

Synthesis mechanism of α-Si3N4 whiskers via SiO vapor in reaction bonded Si3N4-SiC composite

Formation and characterization of α-Si3N4 whiskers from laser synthesized nano amorphous Si_N_C powders

Synthesis of Nano-Alumina Hydroxide Sol Using Sol-gel Method

Preparation of SiC from Water Soluble Phenol-formaldehyde Resin

Synthesis and Characterization of Α-Phase Silicon Nitride Powders by Direct Nitridation

Synthesis and structural characterization of SiO2-Al 2O3 xerogels

Formation Mechanisms of Α-Si3n4 Crystals from Amorphous Si3N4 Powder Synthesized by a Low-Temperature Liquid-Phase Method

Molten Salt Synthesis of Mullite Whiskers from Silicon Carbide Precursor

In-situ synthesis of SiC nanowires on biomass carbon materials derived from cherry stones

The Synthesis and Characterization of SiO_2-Al_2O_3 Xerogels

A Novel Method To Synthesize Amorphous Silica−Alumina Materials with Mesoporous Distribution without Using Templates and Pore-Regulating Agents