Abstract:This study compares the microstructure and tensile properties of Ti6Al4V components fabricated by laser direct metal deposition (LDMD) additive manufacturing (AM) in the transverse and longitudinal directions. The results show anisotropic tensile properties with the transverse direction having high tensile and fracture strengths and the longitudinal direction having a high elongation and reduction of cross section. The anisotropic mechanical properties are attributed to the anisotropic microstructural distribution. The transverse tensile specimen is composed of short columnar prior-β grains which grow perpendicular to the tensile direction, and have a lamellar structure. Along the β grain boundary, αGB and large α colonies were identified. However, the longitudinal specimen shows that the long β structure is parallel to the tensile axis and that the microstructure is composed of basket-woven α phases with shorter α plates and smaller colony sizes compared with those in the transverse specimen. The fracture mechanism induced by the anisotropic microstructure along the transverse and longitudinal directions was compared by examining the fracture process in real-time using uniaxial in-situ scanning electron microscopy (SEM) tensile testing. The results show that shear fracture, which is caused by the vertical β grain boundaries and large α colonies with long α plates, occurs in the transverse specimen. The shear mode is the main reason behind the enhanced tensile strength and fracture strength due to the high resistance to microcrack propagation. However, in the longitudinal specimens, symmetric necking behavior due to the fine α grains resulted in uniform deformation of the grains on both sides of the grain boundaries, inducing greater elongation.

Microstructure and mechanical properties of laser melting deposited γ-TiAl intermetallic alloys

The effects of heat treatment on the microstructure and mechanical property of laser melting deposition γ-TiAl intermetallic alloys

Investigation on the Microstructure and Mechanical Behaviors of a Laser Formed Nb-Ti-Al Alloy

In-situ Investigation of the Anisotropic Mechanical Properties of Laser Direct Metal Deposition Ti6Al4V Alloy

Microstructure and Mechanical Property of Laser Melting Deposition (lmd) Ti/Tial Structural Gradient Material

Microstructure and Mechanical Properties of Ti-6al-4v Components Fabricated by Laser Micro Cladding Deposition

Study of microstructure and compressive strength of a novel Ti-0.75Al-9.5V alloys manufactured by laser deposition melting

In-Situ Tensile Deformation Behavior Of As-Built Laser Direct Metal Deposited Ti-6al-4v Alloy At 200 Degrees C

The Microstructure and Mechanical Behaviors of the Ti–6.5Al–3.5Mo–1.5Zr–0.3Si Alloy Produced by Laser Melting Deposition

Microstructure And Tensile Properties Of Laser Melting Deposited Ti-5al-5mo-5v-1cr-1fe Near Beta Titanium Alloy

Chemical, microstructure, and mechanical property of TiAl alloys produced by high-power direct laser deposition

Microstructural evolution and mechanical properties of laser melting deposited Ti–6.5Al–3.5Mo–1.5Zr–0.3Si titanium alloy

Microstructure Evolution and Mechanical Behavior of Al–Li Alloy Fabricated by Laser Melting Deposition Technique

Effect of thermal exposure on microstructure and tensile properties of laser deposited Ti60A alloy

Microstructure and Mechanical Properties of Laser Metal Deposited Ti6Al4V Alloy with Near Equiaxed Β Grain Structure

Anisotropic Tensile Behavior of Ti-47Al-2Cr-2Nb Alloy Fabricated by Direct Laser Deposition

Microstructure Characteristics and Failure Mechanisms of Ti-48Al-2Nb-2Cr Titanium Aluminide Intermetallic Alloy Fabricated by Directed Energy Deposition Technique

Microstructure Evolution and Mechanical Properties of Laser Additive Manufactured Ti–5Al–2Sn–2Zr–4Mo–4Cr Alloy

Hot Tensile Deformation Behavior of Ti-6Al-4V Titanium Alloy Made by Laser Melting Deposition

Microstructure and Mechanical Properties of As-Deposited and Heat Treated Ti–5Al–5Mo–5V–3Cr–1Zr (Ti-55531) Alloy Fabricated by Laser Melting Deposition

Investigation on solid-state phase transformation in a Ti-47Al-2Cr-2V alloy due to thermal cycling during laser additive manufacturing process