Abstract:TiO2-ZrO2 (Ti-Zr) carrier was prepared by a co-precipitation method and 1 wt. % V2O5 and 0.2 CeO2 (the Mole ratio of Ce to Ti-Zr) was impregnated to obtain the V2O5-CeO2/TiO2-ZrO2 catalyst for the selective catalytic reduction of NOx by NH3. The transient activity tests and the in situ DRIFTS (diffuse reflectance infrared Fourier transform spectroscopy) analyses were employed to explore the NH3-SCR (selective catalytic reduction) mechanism systematically, and by designing various conditions of single or mixing feeding gas and pre-treatment ways, a possible pathway of NOx reduction was proposed. It was found that NH3 exhibited a competitive advantage over NO in its adsorption on the catalyst surface, and could form an active intermediate substance of -NH2. More acid sites and intermediate reaction species (-NH2), at lower temperatures, significantly promoted the SCR activity of the V2O5-0.2CeO2/TiO2-ZrO2 catalyst. The presence of O2 could promote the conversion of NO to NO2, while NO2 was easier to reduce. The co-existence of NH3 and O2 resulted in the NH3 adsorption strength being lower, as compared to tests without O2, since O2 could occupy a part of the active site. Due to CeO2’s excellent oxygen storage-release capacity, NH3 adsorption was weakened, in comparison to the 1 wt. % V2O5-0.2CeO2/TiO2-ZrO2 catalyst. If NOx were to be pre-adsorbed in the catalyst, the formation of nitrate and nitro species would be difficult to desorb, which would greatly hinder the SCR reaction. All the findings concluded that NH3-SCR worked mainly through the Eley-Rideal (E-R) mechanism.

Comparative Study on V-W/TiO2/γ-Al2O3 for Selective Catalytic Reduction of NO

Catalytic performance of MnO 2-CeO 2/Ti 0.25Zr 0.25Al 0.5O 1.75 monolith catalyst for low temperature selective catalytic reduction of NO with NH 3

In Situ DRIFTS Studies of NH3-SCR Mechanism over V2O5-CeO2/TiO2-ZrO2 Catalysts for Selective Catalytic Reduction of NOx

Enhanced Catalytic Performance of V2O5–WO3/Fe2O3/TiO2microspheres for Selective Catalytic Reduction of NO by NH3

Activation of Fast Selective Catalytic Reduction of NO by NH3 at Low Temperature over TiO2 Modified CuOX-CeOX Composites

Performance of V_2O_5-WO_3-MoO_3/TiO_2 Catalyst for Selective Catalytic Reduction of NO_x by NH_3

Experimental Study on Preparation of V_2O_5-WO_3-MoO_3/TiO_2 Catalysts and Selective Reduction of NO_x with NH_3

Highly Efficient Mesoporous V2O5/WO3–TiO2 Catalyst for Selective Catalytic Reduction of NOx: Effect of the Valence of V on the Catalytic Performance

Performance of V2o5-Wo3-Moo3/Tio2 Catalyst for Selective Catalytic Reduction of Nox by Nh3

Investigations of Surface VOx Species and Their Contributions to Activities of VOx/Ti0.5Sn0.5O2 Catalysts Toward Selective Catalytic Reduction of NO by NH3

Insight into the catalytic performance and NH3 adsorption under high concentration of CO2 and/or H2O conditions on selective catalytic reduction of NO by NH3 over V2O5-WO3/TiO2 catalyst

Effect of Synthesis Methods on Activity of V2O5/CeO2/WO3-TiO2 Catalyst for Selective Catalytic Reduction of NOx with NH3

Nh3 Selective Catalytic Reduction of No: A Large Surface Tio2 Support and Its Promotion of V2o5 Dispersion on the Prepared Catalyst

V2O5-WO3/TiO2 Catalysts for Low Temperature NH3 SCR: Catalytic Activity and Characterization

Highly dispersed V2O5/TiO2 modified with transition metals (Cu, Fe, Mn, Co) as efficient catalysts for the selective reduction of NO with NH3

Promotion Effect of Tungsten Oxide on SCR of NO with NH3 for the V2O5–WO3/Ti0.5Sn0.5O2 Catalyst: Experiments Combined with DFT Calculations

V<sub>2</sub>O<sub>5</sub>-WO<sub>3</sub>/TiO<sub>2</sub> Catalysts for Low Temperature NH<sub>3</sub> SCR: Catalytic Activity and Characterization

Catalytic Reduction of NO with NH 3 over V 2 O 5 -MnO X /TiO 2 -Carbon Nanotube Composites

SO2 Promoted V2O5-MoO3/TiO2 Catalyst for NH3-SCR of NOx at Low Temperatures

Substitution of WO3in V2O5/WO3–TiO2by Fe2O3for Selective Catalytic Reduction of NO with NH3

Synthesis of TiO2/γ-Al2O3 and Effect of CuO Loading on NO Reduction