Abstract:(Cu,C)Ba2Ca3Cu4Oy is a nontoxic cuprate superconducting material with a superconducting transition temperature of about 116 K. Recently, it was found that bulk samples of this material synthesized under high pressure hold the highest irreversibility line among all the superconductors, which is very promising for its application in the liquid nitrogen temperature field. In this work, high-temperature (Cu,C)Ba2Ca3Cu4Oy superconducting films with large irreversible fields were prepared on SrLaAlO4(00l) substrates by pulsed laser deposition. The substrate temperature during deposition proved to be the most important parameter determining the morphology and critical temperature of the superconductors, with 680 °C considered to be the optimum temperature. X-ray diffraction (XRD) results showed that the (Cu,C)Ba2Ca3Cu4Oy films prepared under optimal conditions exhibited epitaxial growth with the a-axis perpendicular to the film surface and the b- and c-axes parallel to the substrate, with no evidence of any other orientation. In addition, resistivity measurements showed that the onset transition temperature (Tconset) was approximately 116 K, the zero-resistance critical temperature (Tc0) was around 53 K, and the irreversible field (Hirr) was about 9 T at 37 K for (Cu,C)Ba2Ca3Cu4Oy films under optimal temperature. This is the first example of the successful growth of superconducting (Cu,C)Ba2Ca3Cu4Oy films on SrLaAlO4(00l) substrates. This will facilitate high-performance applications of (Cu,C)Ba2Ca3Cu4Oy superconducting materials in the liquid nitrogen temperature field.

Preparation of superconducting HgBa2CaCu2Ox films with a zero-resistance transition temperature of 121 K

Preparation of Superconducting HgBa2CaCu2Ox and Hg0.8Bi0.2Ba2CaCu2Ox Films by Means of Annealing of Mercury-Free Precursor Films

Synthesis of the Superconducting Thin Film of HgBa2Ca2Cu3O8+δ

Fabrication of Highly -Axis Oriented Hg - Pb - Ba - Ca - Cu - O Thin Films

Synthesis and Properties of the Hg-1223 Superconducting Thin Films Prepared by Ion Implantation

Highly Oriented HgBaCaCuO Superconducting Thin Films Prepared by Laser Ablation

Superconducting Thin Films of (cu,c)ba2ca2cu3o9±δ with Zero-Resistance Transition Temperature Close to 100 K

Bulk Processing of HgBaCuO High T/sub C/ Superconductors by a Two-Zone Technique

Synthesis And Thermal Stabilization Of Nearly Single-Phase Superconductor Hgba2ca2cu3o8+Delta By Tl Substitution

Thin-Films Bi(Pb)-Sr-Ca-Cu-O (tc(zero)=105k) Prepared by Ion-Beam Sputtering

Superconducting thin films of (Cu,C)Ba$_2$Ca$_2$Cu$_3$O$_{9+δ}$ with zero resistance transition temperature close to 100 K

Preparation and Superconducting Properties of the (cu,c)ba2ca3cu4o11+y Films with Zero-Resistance Transition Temperature of 96 K

High Tc Superconducting HgBa2CaCu2Oy Films Growth on the YZrO2 Substrates with YBa2Cu3O7 Buffer Layers

Synthesis and Magnetic Characterization of the High-Tc Superconducting Compound HgBa2CuO4+δ

The Synthesis and Characterization of HgBa2Ca2Cu3O8+δ Superconductors with Substitution of Hg by Pb

Synthesis and Characterization of Heavily Overdoped Tl2Ba2CuO6+δ Thin Films

Phase transition of the HgBa2Ca2Cu3O8 superconducting phase by in-situ heating in transmission electron microscope

Superconductivity at 94 K in HgBa2Cu04+δ

Syntheses and Neutron Powder Diffraction Studies of the Superconductor HgBa2Ca2Cu3O8+δ by Pb Substitution

Crystal Growth and Characterization of HgBa2Ca2Cu3O8+δ Superconductor with the Highest Critical Temperature at Ambient Pressure

High-Temperature (Cu,C)Ba2Ca3Cu4Oy Superconducting Films with Large Irreversible Fields Grown on SrLaAlO4 Substrates by Pulsed Laser Deposition