Realization of Modulating Broadband Emission from Er–Tm Codoped Calcium Boroaluminate Glasses by Dual-Wavelength Pumping
Mingzhu Li,Fang Lu,Fei Xu,Zuimin Jiang,Xiao Wang,Haonan Lou,Zhongquan Ma,Lingling Zheng
DOI: https://doi.org/10.1016/j.matchemphys.2012.09.020
IF: 4.778
2012-01-01
Materials Chemistry and Physics
Abstract:Near-infrared photoluminescence (PL) of calcium boroaluminate (CABAL) glasses codoped with Er2O3 and Tm2O3 has been investigated by dual-wavelength pumping at 795 and 476 nm. Spectrum shape of broadband emission could be modulated by controlling the power ratio of two pumping lines (P-476/P-795). The result shows that the full width at half maximum can reach similar to 500 nm in the wavelength range from 1.3 to 2.0 mu m by controlling P-476/P-795 = 12. The PL spectra show four characteristic peaks located at 1.46, 1.53, 1.58 and 1.80 mu m, corresponding to Tm3+: H-3(4) -> F-3(4), Er3+: I-4(13/2) -> I-4(15/2), Tm3+: (1)G(4) -> F-3(2) and Tm3+: F-3(4) -> H-3(6) emissions, respectively. The energy transfer (ET) (ET1: Er3+: I-4(13/2), Tm3+: F-3(4) -> Er3+: I-4(15/2), Tm3+: H-3(4) and ET2: Er3+: I-4(13/2), Tm3+: H-3(6) -> Er3+: I-4(15/2), Tm3+: F-3(4)) between Er3+ and Tm3+ ions play important roles in the luminescence mechanisms. In addition, a new ET process (ET: Tm3+: (1)G(4), Er3+: F-4(9/2) -> Tm3+: F-3(2), Er3+: F-4(7/2)) was identified. The flat broadband emission with the bandwidth of similar to 500 nm could be realized by changing P-476/P-795 as a result of the radiative transitions, Tm-Tm cross-relaxation (Tm3+: H-3(4), H-3(6) -> Tm3+: E-3(4), F-3(4)) and Er-Tm ET processes. (C) 2012 Elsevier B.V. All rights reserved.