Abstract:Arrays of randomly oriented zinc oxide (ZnO) nanowires were fabricated on silicon wafers via a simple thermal evaporation method. During the fabrication, the temperature around the substrate was below 500°C. The products were analyzed by conventional means and determined to be single crystals of wurtzite-type ZnO that grew along the c-axis. These nanowires were 10–100nm in diameter and 10–100μm in length, suggesting a possible high field enhancement factor. The dependence of the field emission current on the anode–cathode voltage (I–V behavior) of the ZnO nanowire arrays was measured in a lab-built ultrahigh vacuum system with a base pressure of 10−7Pa. After surface cleaning by heat treatment, two characteristic electric fields, under which 10μA/cm2 and 1mA/cm2 current densities were extracted, were measured to be 4.0 and 4.7V/μm, respectively. As observed with a transparent anode, emission occurred uniformly over the whole sample surface. A 72h-long test on emission stability was performed under a constant voltage of 2.75kV. The current dropped occasionally to approximately 80% of the initial value during the test owing to the poor adherence of the nanowires to the substrate. These preliminary results have shown the perspective of, as well as a major drawback to, a ZnO nanowire array being developed into a cold electron source to be used in future electronic devices.

Improving Field-Emission Uniformity of Large-Area W18O49 Nanowire Films by Electrical Treatment

Improvement of Field Emission Uniformity of Tungsten Oxide Nanowire Arrays Via In-Situ Plasma Treatment

Controlled synthesis of patterned W18O49 nanowire vertical-arrays and improved field emission performance by in situ plasma treatment

Stable, Self-Ballasting Field Emission from Zinc Oxide Nanowires Grown on an Array of Vertically Aligned Carbon Nanofibers

Enhanced Field Emission from Large-Area Arrays of W18o49 Pencil-Like Nanostructure

Enhanced Field Emission from Large-Area Arrays of W <sub>18</sub> O <sub>49</sub> Pencil-Like Nanostructure

High FE current density from tungsten oxide nanowires

Field-Emission Properties of Nanostructured Wo3 Arrays Fabricated Using Tungsten Hot-Filament Chemical Vapor Deposition

Study of Techniques for Improving Emission Uniformity of Gated Cuo Nanowire Field Emitter Arrays

Defect-Enhanced Field Emission from WO3 Nanowires for Flat-Panel X-ray Sources

Extremely Stable Field Emission from AlZnO Nanowire Arrays

Fabrication of patterned aligned W18O49 nanowire arrays with high field emission performances

A novel lift-off method for fabricating patterned and vertically-aligned W18O49 nanowire arrays with good field emission performance.

On Achieving Better Uniform Carbon Nanotube Field Emission by Electrical Treatment and the Underlying Mechanism

WO3 nanowire field emission point electron source with high brightness and current stability

Fabrication of Large-Area ZnO Nanowire Field Emitter Arrays by Thermal Oxidation for High-Current Application

Field Emission Microscopy Study of Zinc Oxide Nanowires on Tungsten Tip

Optimization Of Field Emission Properties Of Gated Cuo Nanowire Field Emitter Arrays For Field Emission Display Application

Change in crystalline structure of W18O49 nanowires induced by X-ray irradiation and its effects on field emission

Anomalous Temperature Dependence Of Field Emission From W18o49 Nanowires Caused By Surface States And Field Penetration

Field Emission Properties of Zinc Oxide Nanowires Fabricated by Thermal Evaporation