Laser Induced Damage Morphology of K9 Glass with Nanosecond Pulse
韩敬华,冯国英,杨李茗,张秋慧,刘民才,杨丽茹,朱启华,谢旭东
DOI: https://doi.org/10.3969/j.issn.1007-2276.2010.01.008
2010-01-01
Infrared and Laser Engineering
Abstract:The characteristics of nanosecond pulsed laser induced damage(LID) in K9 glass were experimentally studied,and the corresponding damage characteristics based on the principle of the interaction between the plasma shock wave and the glass were analyzed as well.The characteristics of the surface damage were that the LID on the surface didn′t occur at low incident energy.With the laser pulse energy increasing,the pit shape of LID would occur.In the center of the pit,there was a core,which corresponded to the bulk damage.Around the core was the melting region,and the outermost zone was the annular fault region.The characteristics of the bulk damage were that the damage shape was like a spindle along the laser propagation direction,and there was filamentary of plasma channel in the central area,whereas the surrounding areas were melting region,region of varying refractive index and the fracture distribution area.In the central areas of the laser-supported detonation wave induced by the Gaussian laser pulse,the motion velocity was the fastest and the pressure was the strongest since the temperature was the highest.So on the inner surface of the glass action effect of the shock wave became weaker from inside to outside,exhibiting radial distribution.However,as for the characteristics of the bulk damage,it was decided by the law of expansive action of shock wave,which became lower from inside to outside.