Abstract:Silicon carbide (SiC) nanopowders were synthesized under Ar atmosphere via the carbonization reaction method using silicon powders and expanded graphite as initial materials, and ferric nitrate as catalyst precursor. The effects of heat treatment temperature and the C/Si molar ratio on SiC products were studied. The microstructure, phase composition and chemical state of the products were analyzed by XRD, SEM, XPS, TEM and Raman. The photoluminescence (PL) properties of SiC nanopowders were tested. The results showed that the content of the 3C–SiC product is higher after heat treatment at 1400 °C for 3 h with a molar ratio of C/Si of 1:1. 3C–SiC exists in the form of particles and wires. The formation process of 3C–SiC can be explained by a two-step method, nucleation under catalysis and growth under Vapor-Solid (VS) mechanism. Two ultraviolet light emission peaks are observed at about 318 and 380 nm. The main PL spectra of 3C–SiC nanopowders exhibit larger blueshifts. The blueshift is attributed to the stacking fault, oxygen defects, morphology and quantum confinement effect. It has potential application prospects in ultraviolet detectors, optoelectronic devices and light emitters.

The synthesis and ultraviolet photoluminescence of 6H–SiC nanowires by microwave method

Ultrafast growth of single-crystalline Si nanowires

Synthesis and Raman Spectra of Si-Nanowires

Molten-salt-mediated synthesis of SiC nanowires for microwave absorption applications

Tiny SiO2 nano-wires synthesized on Si (111) wafer

Photoluminescence property of inexpensive flexible SiC nanowires membrane by electrospinning and carbothermal reduction

Tiny SiO2 nano-wires synthesized on Si (1 1 1 ) wafer

Synthesis and Properties of Sic/Sio2 Nanochain Heterojunctions by Microwave Method

Tiny silicon nano-wires synthesis on silicon wafers

Preparation of 2H/3C–SiC heterojunction nanowires from molten salt method with blue shift photoluminescence property

Tuning the morphologies of SiC nanowires via the control of growth temperature, and their photoluminescence properties.

Large-scale synthesis and characterization of hexagonal prism-shaped SiC nanowires.

Controlled Al-Doped Single-Crystalline 6H-Sic Nanowires

Synthesis, Structure and Photoluminescence of Twinned SiC Nanowires

Triangular prism-shaped p-type 6H-SiC nanowires

Synthesis of the tube-brush-shaped SiC nanowire array on carbon fiber and its photoluminescence properties.

The synthesis and photoluminescence properties of selenium-treated porous silicon nanowire arrays.

Synthesis and Photoluminescence Properties of Porous Silicon Nanowire Arrays

Synthesis and investigation of the physicochemical properties of polymorphic 3C–SiC

Tunable Violet–blue Emission from 3C-Sic Nanowires

In-situ growth of SiC nanowire arrays on carbon fibers and their microwave absorption properties