Refinement of TiB2 Powders with High-speed Planetary Mill and Its Effect on TiB2 Sinterability
Qiwei Huang,Ruomeng Ai,Wenhui Bai,Qianglong He,Aiyang Wang,Lanxin Hu,Weimin Wang
DOI: https://doi.org/10.1007/s11595-021-2413-y
2021-06-01
Abstract:<p class="a-plus-plus">Titanium diboride ceramic was produced via spark plasma sintering (SPS) using finer TiB<sub class="a-plus-plus">2</sub> powder made by high-speed planetary ball milling. The effects of ball milling parameters on the composites and particle size of TiB<sub class="a-plus-plus">2</sub> powder were investigated. It was shown that the average particle size of TiB<sub class="a-plus-plus">2</sub> powder decreased from 5.8 to 1.59 µm and the wear rate of WC balls was 1.58 wt%, when the ball-to-powder weight ratio (BPR), the rotary speed and milling time and were 10:1, 600 rpm and 20 min, respectively. The content of WC in TiB<sub class="a-plus-plus">2</sub> powder can be limited below 4.58 vol% by optimizing the milling conditions. The sintering temperature of TiB<sub class="a-plus-plus">2</sub> powder milled can be decreased obviously, and the mechanical properties are evidently improved and the microstructure becomes more homogeneous when the powder of TiB<sub class="a-plus-plus">2</sub> becomes finer. The relative density, hardness, bending strength, and fracture toughness of the TiB<sub class="a-plus-plus">2</sub> ceramic fabricated at 1 700 °C reach the optimal values, which are 98.13%, 19.14 GPa, 756 MPa, and 5.71 MPa·m<sup class="a-plus-plus">1/2</sup>, respectively. The decrease of TiB<sub class="a-plus-plus">2</sub> particle size and the introduction of WC are the potential reasons for the improvement of TiB<sub class="a-plus-plus">2</sub> ceramic performance.</p>
English Else