Abstract:Single-crystal nickel-based CMSX-6 superalloy rods were directionally solidified at a constant withdrawal rate by employing a novel directional solidification process the downward directional solidification process and the Bridgman process. For the rods cast using both processes, the local cooling rates were measured at the 5.5 cm and 12.5 cm locations between the solidification front and the chill end. With an increasing distance from the chill, the cooling rate varied from 1.21 to 1.08 K/s giving a change in the rate of 10.74% in the novel process. In contrast to this, the cooling rates in the Bridgman process varied from 0.15 to 0.08 K/s giving a change in the rate of 46.67%. The microstructural evolution was comparatively investigated for the two processes as a function of the cooling rates. In comparison to the Bridgman process, refined gamma dendrite structures, smaller size of gamma/gamma' eutectic island, refined gamma' precipitates in the dendritic core and a smaller average size of microporosities were observed in both locations of the rods cast by using the novel process. In addition to this, the variations of the primary and secondary dendrite arm spacings, the size of gamma/gamma' eutectic island, and the size of gamma' precipitates in the dendrite core were smaller than those in the Bridgman process with increasing the distance from 5.5 cm to 12.5 cm. This indicates that the downward directional solidification process can cast a rod possessing more homogeneous microstructures. Moreover in comparison to the Bridgman process, the majority of the micropores have smaller diameters and both the variation in the maximum size of microporosity as well as the average diameter of these micropores located between positions near to the chill end and the distant end were smaller in the rods cast by using the novel process; the opposite is found in the Bridgman process. (C) 2014 Elsevier B.V. All rights reserved.

Microstructure and Stress Rupture Properties of Single Crystal Superalloy CMSX-2 under High Thermal Gradient Directional Solidification

Effect of Directional Solidification Methods on Solid Solution Window in Ni-based Single-Crystal Superalloy

MICROSTRUCTURE AND MICROSEGREGATION OF Ni-BASE SINGLE CRYSTAL SUPERALLOY SOLIDIFIED AT MEDIUM COOLING RATE

A High Thermal Gradient Directional Solidification Method for Growing Superalloy Single Crystals

Directional Solidification Behavior of CMSX-6 Superalloy

Solidification and microsegregation behaviors of nickel-base single crystal superalloy solidified at medium cooling rate

Microstructure and Microsegregation in A Ni-Based Single Crystal Superalloy Directionally Solidified under High Thermal Gradient

Characterization of the Microstructure Evolution and Microsegregation in A Ni-Based Superalloy under Super-High Thermal Gradient Directional Solidification

Processing, Microstructures and Mechanical Properties of a Ni-Based Single Crystal Superalloy

Superfine dendrite and microsegregation of Ni-base single crystal superalloy

Temperature Effects on Deformation Substructures and Mechanisms of a Ni-based Single Crystal Superalloy

Effect of Local Cooling Rates on the Microstructures of Single Crystal CMSX-6 Superalloy: A Comparative Assessment of the Bridgman and the Downward Directional Solidification Processes

Directional solidification of a Ni-based single crystal superalloy under high temperature gradient

Influence of directional solidification variables on the microstructure and crystal orientation of AM3 under high thermal gradient

Effect of the Cooling Rate on the Microstructure of Directionally Solidified Casting (CMSX-4 Ni Superalloy)

Ultra high-temperature deformation in a single crystal superalloy: Meso-scale process simulation and micro-mechanisms

Microstructure and Elevated Temperature Tensile Behaviour of Directionally Solidified Nickel Based Superalloy

Effect of Solidification Parameters on the Microstructures of Superalloy CMSX-6 Formed During the Downward Directional Solidification Process

On Morphologies, Microsegregation, and Mechanical Behavior of Directionally Solidified Cobalt-Base Superalloy at Medium Cooling Rate

On the directional solidification processing for super-refinement of submicrostructure of single crystal superalloy DD3

Influence of Processing Parameters on the Solidification Behavior of Single-Crystal Cmsx-4 Superalloy