MODELING AND SIMULATION OF DIRECTIONAL SOLIDIFICATION BY LMC PROCESS FOR NICKEL BASE SUPERALLOY CASTING
Yan Xuewei,Tang Ning,Liu Xiaofu,Shui Guoyan,Xu Qingyan,Liu Baicheng
DOI: https://doi.org/10.11900/0412.1961.2015.00338
IF: 1.797
2015-01-01
ACTA METALLURGICA SINICA
Abstract:Gas turbine plays an important role in energy and aviation, among which the turbine blades are the key components. Ni base superalloys are the preferred material to manufacture blades due to their high temperature strength, microstructural stability and corrosion resistance. As a conventional directional solidification method, high-rate solidification (HRS) is used to produce columnar grain and single crystal blades. However, there are several problems when FIRS is scaled to cast industrial gas turbines (KIT) components. In recent years, several possible techniques are being proposed for large IGT blades. The liquid-metal cooling (LMC) is one of the best methods among them, which improves heat extraction by immersing the casting and the mold into a container of metal cool-ant with low melting temperature as they are withdrawn from the heating zone. Unfortunately, the trial and error method is time and money cost and lead to a long R&D cycle. Therefore, numerical simulation plays an important role to optimize the process, and enhance the productivity in LMC directional solidification. In this work, mathematical models for dynamic heat radiation and convection boundary of LMC process are established to simulate the temperature fields. Cellular automaton (CA) method and KGT growth model are used to describe the nucleation and growth. The pouring experiments are carried out. The accuracy of the model is validated by the cooling curves and microstructure. Moreover, the liquid-metal cooling directional solidification process is discussed in more detail, including primary dendrite arm space (PDAS), secondary dendrite arm space (SDAS), mushy zone and microstructure, etc.. Simulation and experiment results are compared in the work. This study indicates that simulation and experimental results agree with each other well. The maximum error of temperature is less than 5 percent and the morphologies of grains are similar. The withdrawal rate has an important influence on the shape of mushy zone and dendritic structure. A concave mushy zone is formed and the grain tends to convergent under an excessive withdrawal rate. However, the mushy zone has a convex shape and the grain is divergent under a smaller withdrawal rate. A proper withdrawal rate is found to obtain smooth mushy zone, improve the parallelism of grains, and refine the dendritic structure.