Preparation of Porous Anatase Titania Film

GX Tang,RJ Zhang,YN Yan,ZX Zhu

DOI: https://doi.org/10.1016/j.matlet.2003.11.016

IF: 3

2004-01-01

Materials Letters

Abstract:A porous anatase titania film was prepared by a composite oxidation method on pure titanium surfaces, which was in a combination of pre-anodic oxidation and micro-arc oxidation treatment. In the pre-anodic oxidation treatment, the sample was immersed in oxalic acid solution using a DC power supply. In micro-arc oxidation treatment, the sample was put into β-glycerophosphate di-sodium salt and calcium acetate electrolytic solution by using an asymmetry pulse power supply. X-ray diffraction (XRD) and scanning electron microscopy (SEM) with EDS spectrum instrument were employed to characterize the phase, composition and microstructure of the film. A micro-hardness tester was employed to test the hardness of the formed film and a scratching machine to evaluate the bond strength of the film. XRD indicated that the film formed by pre-anodic oxidation was composed of a thin anatase film, which was uniform and even. While the film prepared by micro-arc oxidation treatment was porous and uneven, with a porous size of 1–3 μm. XRD showed that the porous film was also made up of anatase. The micro-hardness of the porous film was 645 HV0.2 and the bond strength of the porous film 36.3 N. The formed film is expected to have significant applications as medical implants.