Influences of Tensile Deformation Rate on Deformation and Morphology of Injection Molded 15/85 (by Weight) Pc/Pe and Pet/Pe Blends with High Interfacial Contact
ZM Li,W Yang,BH Xie,R Huang,MB Yang,JM Feng
DOI: https://doi.org/10.1081/mb-120029786
2004-01-01
Abstract:Through the lower-melting temperature component processing (LTCP) of the blends (where the processing temperature of the lower-melting temperature component in a blend is used), high interfacial contact (pseudo-adhesion) in poly(ethylene terephthalate) (PET)/polyethylene (PE) and polycarbonate (PC)/PE blends is obtained from the difference in the contraction of the dispersed particles and the matrix during cooling from the processing temperature to room temperature. As a result of the pseudo-adhesion, the tensile strength and modulus of the PET/PE and PC/PE blends with high interfacial contact are superior to those of their corresponding classical blends and, additionally, the PC reinforcement on the matrix is more noticeable than the PET. Morphological observation indicates that during uniaxial deformation at a tensile rate of 50 mm/min, numerous PC microfibers are in situ formed in the PC/PE blend, whereas in the PET/PE blend, ellipsoidal particles appear, resulting from slippage taking place between the PET particles and the matrix. When the tensile rate is higher or less than 50 mm/min, the extent of plastic deformation for both PC and PET particles reduces. During elongation, for the PET/PE blend, necking first takes place at a point close to the non-gate end of the specimens; subsequently the necking (cold drawing) spreads uniformly from this point at tensile rates of 10 and 50 mm/min. On the other hand, for the PC/PE blend at these two tensile rates, the position of the necking zone and the necking extension are irregular, and generally, the whole zone between the two grips is deformed gradually. As the tensile rate is increased to 300 mm/min, both blends fracture in a brittle manner.