Abstract:Cerium dioxide (CeO2) nanoparticles were synthesized by sol–gel-based hydrothermal method. During synthesis, cerium(III) chloride heptahydrate (CeCl3⋅7H2O) was used as cerium source; ammonia (NH3), tetraethylammonium hydroxide (C8H21NO), tetra-n-butyl ammonium hydroxide (C16H37NO), benzyl trimethyl ammonium hydroxide (C10H17NO) and benzyl triethyl ammonium hydroxide (C13H23NO) ionic liquids were used as catalyst, deionized water (H2O) was used as hydrolysis agent and solvent, and 2-aminopropanoic acid (C3H6NO2) was used as stabilizing agent. The nano-CeO2 particles were characterized by several techniques X-ray diffractometer (XRD), particle size analyzer, Branauer–Emmett–Teller analyzer (BET), ultraviolet–visible spectrophotometer (UV–Vis), transmission electron microscope (TEM). XRD characterization confirms that CeO2 crystals were analyzed as cubic fluorite structure. The full width at half maximum (FWHM) values referring to [111] lattice planes of CeO2 indicate a decrease in crystallinity associated with different bases used during synthesis of particles. Small sized crystals were formed in weak ionization degree and branched structures. As the crystallite size decreases, both agglomeration and the hydrodynamic diameter increases as expected. The size distribution of nano-CeO2 particles obtained by precipitation using different bases with a pH of 10 decreases from 25.92 to 20.57 nm. The size of nanoparticles prepared using ammonia at pH 9 and 8 are 15.60 and 9.50 nm, respectively. The most significant surface area change occurred in particles obtained using benzyl trimethyl ammonium hydroxide (BTMAH) and benzyl triethyl ammonium hydroxide (BTEAH). Such a significant reduction in surface area is believed to be due to the agglomeration or aggregation of particles with small crystallite size, resulting in smaller sized crystals as the alkyl group chain length and branching increase. These irregularities may result from the agglomeration and formation of large clusters observed by the TEM. The obtained CeO2 nanoparticles are crystalline and can readily be dispersed in water without any additional processing or surfactant agent. Well-defined strong absorbance peak located at 200–800 nm was observed for all samples. The bandgap increases with the decrease in particle size, meaning that smaller particles exhibit better UV absorption. The fact that the particles obtained in the presence of BTMAH and BTEAH cut off longer wavelength proved that it is due to lower bandgap energies.Graphical abstract

Preparation of Discrete Nanosize Ceria Powder

Preparation of Nanocrystalline Ceria Particles by Sonochemical and Microwave Assisted Heating Methods

Preparation of nano-sized CeO2 by mechanochemical reaction of cerium carbonate with sodium hydroxide

Characterization of CeO 2 Fine Particles Prepared by the Homogeneous Precipitation Method with a Mixed Solutionof Ethylene Glycol and Polyethylene Glycol

Wet chemical preparation of well-dispersed colloidal cerium oxide nanocrystals

Preparation of Monodispersed Nanocrystalline Ceo2 Powders by Microwave Irradiation

Synthesis and characterization of ceria nanoparticles by complex-precipitation route

Preparation of ceria by combined sol–gel and hydrothermal method: insights from the effects of different bases on the particle size distribution

Novel Azeotropic Distillation Process for Synthesizing Nanoscale Powders of Yttria Doped Ceria Electrolyte

PREPARATION OF ULTRAFINE CeO_2 PARTICLES BY USING DIFFERENT METHODS II.Frozen Dehydrating Method and Urea Decomposition Method

Synthesis Of Ceo2 Spherical Fine Particles By Homogeneous Precipitation Method With Polyethylene Glycol

Preparation of Nanometer Cerium Oxide by Microwave Irradiation and Study on Its Surface Modification

Synthesis and Characterization of Doped Nano-Sized Ceria–zirconia Solid Solutions

A Novel Method To Prepare Nanocrystalline (7 Nm) Ceria

INFLUENCE OF PRECIPITANTS ON STRUCTURE OF COLLOIDAL SOLUTION SPRAY PYROLYSIS DERIVED Sm_(0.2)Ce_(0.8)O_(1.9) SOLID ELECTROLYTE

Preparation and Characterization of CeO<sub>2</sub> with Different Particle Sizes and Morphology

Preparation of Ceria with Large Particle Size and High Appearance Density

Low-Temperature Preparation of Dense 10 Mol%-Y2o3-Doped Ceo2 Ceramics Using Powders Synthesized Via Carbonate Coprecipitation

Synthesis of Nanocrystalline Ce<sub>0.8</sub>Sm<sub>0.2</sub>O<sub>1.9</sub> by Citrate Gel Method

Hydrothermal synthesis of CeO2 nano-particles

Synthesis of Nanocrystalline Ce0.8sm0.2o1.9 by Citrate Gel Method