Abstract:Tungsten and tungsten alloys are widely used in high temperature environments where arc ablation or mechanical deformation and damage are the main sources of materials failure. For high temperature critical applications in thermomechanical environments, however, the low strength limits the use of tungsten and tungsten alloys. Hence, new tungsten based materials with good high temperature thermomechanical properties need to be developed in order to extend the use of tungsten. TiC particle-reinforced tungsten based composites (TiCp/W) were fabricated by hot pressing at 2000 °C, 20 MPa in a vacuum of 1.3×10−3 Pa. The composites were examined with respect to their thermophysical and mechanical properties at room temperature and at elevated temperature. Vickers hardness and elastic modulus increased with increasing TiC content from 0 to 40 vol.%. The highest flexural strength, 843 MPa, and the highest toughness, 10.1 MPam1/2, of the composites at room temperature were all obtained when 20 vol.% TiC particle were added. As the test temperature rose, the flexural strength of the TiCp/W composites firstly increased and then decreased, except in the monolithic tungsten. The highest strength of 1155 MPa was measured at 1000 °C in the composite containing 30 vol.% TiC particles. The strengthening effect of TiC particles on the tungsten matrix is more significant at high temperatures. With the addition of TiC particles, the thermal conduction of tungsten composites was drastically decreased from 153 Wm−1K−1 for monolithic W to 27.9 Wm−1K−1 for 40 vol.% TiCp/W composites, and the thermal expansion was also increased. The new composites are successfully used to make high temperature grips and moulds.

Elevated temperature ablation resistance and thermophysical properties of tungsten matrix composites reinforced with ZrC particles

Influence of Zrc Content on the Elevated Temperature Tensile Properties of Zrcp/W Composites

Ablation of Tungsten Matrix Composites Reinforced by TiC and ZrC Particles

Tungsten Joining with Copper Alloy and Its High Heat Load Performance

Effect of Carbide Particles on the Ablation Properties of Tungsten Composites

High-temperature Erosion of Titanium-Carbide-particle-reinforced Tungsten Composites

Microstructure and Ablation Behavior of W Coating Prepared by Atmospheric Plasma Spraying for Zr/Cu Infiltrated C/C Composites

The Mechanical and Thermophysical Properties of ZrC/W Composites at Elevated Temperature

Microstructure and ablation behaviour of C/C-SiC-ZrC-Cu composites prepared by reactive melt infiltration

Outstanding Mechanical and Ablation Resistance of C/C–ZrC–W Composites Prepared Via Slurry Impregnation and Reactive Melt Infiltration at 1500 ℃

Ablation Properties of ZrCp/W Composites

Elevated Temperature Ablation Mechanisms of Cu@rGO/CuW Nanocomposites under Oxyacetylene Torch Flame

Ablation Resistance of C/C Composites with Atmospheric Plasma-Sprayed W Coating

Oxidative ablation behavior of W‐coated C/C composites prepared by CVD with heat‐treatment

Ablation behaviors of ultra-high temperature ceramic composites

Zirconium Carbide for Hypersonic Applications, Opportunities and Challenges

Carbide Particle-Reinforced Tungsten Composites in Extreme Hazard Environments

Novel low temperature derived W f /W-ZrC-Cu composites by reactive infiltration with enhanced mechanical and thermal physical properties

Anti-ablation properties of ZrB2 modified carbon/phenolic composites in plasma wind tunnel

Mechanical and Ablation Properties of Three-Dimensional ZrC Skeleton Reinforced Graphite-Based Composites

Thermomechanical Properties of TiC Particle-Reinforced Tungsten Composites for High Temperature Applications