Abstract:Inconel 617 nickel-based superalloy with 3 mm wall thickness was welded by laser beam using two different heat input welding parameters. The microstructure of the welded joint was observed by optical microscope and scanning electron microscope, and the mechanical properties of the welded joint at room temperature (25celcius) and high temperature (900celcius) were tested. The results show that the laser welding heat input has a significant effect on the microstructure and mechanical properties of Inconel 617 welded joints. The front width of the laser weld obtained by high heat input (200 J/mm) process parameters is 3.88 mm. The grain size in the middle of the weld fusion zone is coarse, and the grain orientation is disordered. The secondary dendrite arm spacing in the middle of the weld is large (6.71 mu m). The carbide particle size between the dendrites is coarse, and the solidification microsegregation of Mo, Cr alloy elements is serious. The width of heat affected zone is about 0.29 mm. The eutectic structure of gamma+carbide is formed in the grain boundary and grain interior. This is because during the heating process of the welding, the spherical carbide particles and the surrounding austenite in the heat-affected zone liquefy and the eutectic structure is formed during the solidification process after welding. The front width of the laser weld obtained by low heat input (90 J/mm) process parameters is 2.28 mm, the grains inside the weld are columnar which is formed by epitaxial growth along the fusion line and directional solidification along the heat flow direction. The secondary dendrite arm spacing in the middle of the weld is small (2.26 mu m), the carbide particles between dendrites are small, and the width of heat affected zone is about 0.15 mm. The tensile strength test at room temperature (25celcius) shows that the welded joints obtained under high heat input fracture from the middle of the weld, and the tensile strength and elongation decrease, which is caused by the segregation of solid solution elements in the weld. The welded joints obtained under low heat input fracture from the base metal. At high temperature (900celcius), all samples fracture from the base metal, which is due to the weakening of the grain boundary of the base metal at high temperatures.

High temperature tensile properties of laser butt-welded plate of Inconel 718 superalloy with ultra-fine grains

Microstructures and High-Temperature Mechanical Properties of Inconel 718 Superalloy Fabricated via Laser Powder Bed Fusion

Insight into Elongation and Strength Enhancement of Heat-Treated LPBF Ni-based Superalloy 718 Using In-Situ SEM-EBSD

Effect of heat input on microstructure and mechanical properties of laser welded joint of Inconel 617 nickel-based superalloy

In-Situ Tensile Deformation Behavior Of As-Built Laser Direct Metal Deposited Ti-6al-4v Alloy At 200 Degrees C

Tensile and Low‐Cycle Fatigue Behavior of Laser Powder Bed Fused Inconel 718 at Room‐ and High Temperature

Investigation on the influence of heat treatment on Inconel 718 fabricated by selective laser melting: Microstructure and high temperature tensile property

In-situ Study of Microstructure and Mechanical Properties of GH3536 Alloy Manufactured by Selective Laser Melting at 750 °C

Temperature dependence of deformation behavior, microstructure evolution and fracture mechanism of Inconel 625 superalloy

In-situ SEM study of temperature-dependent tensile behavior of Inconel 718 superalloy

Microstructure and mechanical properties at elevated temperatures of as-built and heat-treated Inconel 718 produced through laser powder bed fusion processes

Effect of Welding Speed on Microstructure and Mechanical Properties of Selective Laser Melting Inconel 625 Alloy Laser Welded Joint

Outstanding ductility of flash-butt welded Inconel 718 joints after post-weld heat treatment

High‐Temperature Mechanical Behavior Assessment based on a Developed Constitutive Model of Inconel 718 Fabricated by Selective Laser Melting

Effect of heat treatment on microstructure, precipitation behavior and mechanical properties of Inconel 718 fabricated by laser direct energy deposition

Anisotropic Stress Rupture Properties-Microstructure Relationships in SLM Inconel 718 Alloy

Effect of heat treatment on microstructure and mechanical properties of selective laser melted Inconel 718 alloy

Outstanding Ductility of Flash-Butt Welded Inconel718 Joints after Post-Weld Heat Treatment

Effect of homogenization and solution treatments time on the elevated-temperature mechanical behavior of Inconel 718 fabricated by laser powder bed fusion

Effect of heat treatment on microstructures and mechanical properties of Inconel 718 additively manufactured using gradient laser power

Origin of the anisotropic ductility and the dynamic recrystallization-like deformation behavior of laser powder bed fusion Inconel 625 at elevated temperature