Abstract:In order to broaden SiC particle-reinforced aluminum matrix composites in the applications of high-temperature and high-power electronic devices for electronics packaging, three types of the zinc-containing fillers and a low-frequency/low-amplitude mechanical vibration agitation technology were introduced for brazing of 10 vol.% and 70 vol.% SiCp/Al-MMCs. The effect of Zn element and mechanical vibration agitation on the microstructure of the joints was investigated. The increasing aluminum concentration and the decreasing zinc concentration in the bond seam were confirmed by the microstructure images, weight loss measurements, and EDS results and were attributed to zinc penetration and volatilization. Vaporization of zinc in the liquid filler increased the voids and number of vacancies, which destroyed the arrangement structure of liquid filler, namely, short-range order and long-range disorder, and facilitated the mutual diffusion of other atoms. The joints of 70 vol.% SiCp/A356-MMCs with a shear strength of 16.6 MPa were produced at 480 °C and 0.5 MPa using Zn-25Al-10Ga-9Mg-1Ti interlayer. For 10 vol.% SiCp/A356-MMCs, sound joints with a shear strength of 119 MPa were obtained at 520 °C using the Zn-5Al-4Mg foil. Cracks are initiated from the particle/metal (P/M) interface and subsequently propagated to the matrix/metal (M/M) interface. Mg-Si-rich phases were observed in the bond seam and at the interface of 70 vol.% SiCp/Al-MMCs with different Mg content interlayers, which was also a weak interface for the joint. The results also indicated that the active element Mg in the filler should be controlled to an appropriate content for brazing of high volume fraction composites.

Interface structure changes during vibration liquid phase bonding of SiCp/A356 composites in air

Modelling Behaviour of Oxide Film During Vibration Diffusion Bonding of SiCp/A356 Composite in Air

Interface structure and formation mechanism of vacuum-free vibration liquid phase diffusion-bonded joints of SiCp/ZL101A composites

Interface Structure and Strength of Ultrasonic Vibration Liquid Phase Bonded Joints of Al2O3p/6061Al Composites

Vibration assisted brazing of SiCp/A356 composites: Microstructure and mechanical behaviour

Solidified Microstructure of SiCp/Al Composites Bonds under Ultrasonic Vibration and Their Fracture Characteristics

Behaviors of Oxide Layer at Interface Between Semi-solid Filler Metal and Aluminum Matrix Composites During Vibration

Interfacial Structure and Formation Mechanism in Ultrasonically Aided Liquid Bonding of Al18B4O33/Al Composites in Air

Thermal expansion behavior and performance of VLP diffusion-bonded joints of SiCp/A356 composites

Research on Semi-Solid Stirring Brazing of SiCp/A356 Composites in Air

Ultrasonic effect mechanism on transient liquid phase bonding joints of SiCp reinforced Mg metal matrix composites using Zn-Al-Zn multi-interlayer.

Abnormal Transient Liquid Phase Bondability of High-Volume Fraction SiC Particle-Reinforced A356 Composite for Cu Interlayer and the Interlayer Improvement Routes

Ultrasonic Dissolution of Brazing of 55% SiCp/A356 Composites

Active-Transient Liquid Phase (A-TLP) Bonding of High Volume Fraction SiC Particle Reinforced A356 Matrix Composite

Microstructure, Mechanical Properties, and Bonding Mechanism of Ultrasonic-Assisted Brazed Joints of Sic Ceramics with Znalmg Filler Metals in Air

Interface Structure of Ultrasonic Vibration Aided Interaction Between Zn–Al Alloy and Al2O3p/6061Al Composite

Liquid Phase Diffusion Bonding for SiC Particles Reinforced Aluminum Matrix Composites Using Pure Copper Inter-Layer

Effect of Zn and Mechanical Vibration Agitation on the Microstructure Evolution in Brazed Joint of SiC Particle-Reinforced Aluminum Matrix Composites

Ultrasonic brazing of high fraction volume of SiC particulate reinforced aluminium matrix composites

Microstructural Evolution and Mechanical Properties of the Joint of TiAl Alloys and C/SiC Composites Vacuum Brazed with Ag–Cu Filler Metal

Microstructure Evolution of SiC/SiC Joints During Ultrasonic-Assisted Air Bonding Using a Sn–Zn–Al Alloy