Abstract:Thin Cr films were nitrided during rapid thermal annealing for 3 min in NH3 between 500 and 850°C. Nitridation begins at 500°C and occurs in a layer-by-layer fashion, first forming Cr2N then CrN. At 550°C, Cr2N begins to nitride to CrN despite the existence of unreacted Cr, such that a CrN/Cr2N/Cr structure exists. At 650°C, no unreacted Cr remains and the layer consists of CrN on Cr2N; this configuration remains at 700°C although CrN grew at the expense of Cr2N. At 750°C, the reaction is complete, forming CrN. Oxygen accumulates in front of the growing nitrides until the temperature is high enough to allow redistribution. This occurs at lower temperatures in Cr2N than in CrN, which may be correlated to the enhanced oxidation resistance of CrN. Phase identification was performed by X-ray diffraction, composition determination by Rutherford backscattering spectrometry, and elemental profiling by secondary ion mass spectrometry. Ion beam resonances of the forms 16O(α,α)16O and 14N(α,α)14N provided additional elemental profiling. Vickers microhardness was measured and was observed to increase sharply once a surface nitride had formed, then remained nearly constant upon further annealing.

Benzene-thermal preparation of nanocrystalline chromium nitride

A Benzene-Thermal Synthetic Route to Nanocrystalline Zrn

Low-Temperature Synthesis of Nanocrystalline Titanium Nitride via a Benzene-Thermal Route

A Benzene-Thermal Synthetic Route to Nanocrystalline GaN

Characterization of well-crystallized graphitic carbon nitride nanocrystallites via a benzene-thermal route at low temperatures

Controlled Synthesis of Novel Chromium Nitride Dendritic and Bundle-Like Nanocrystals Via Solvent-Free Route at Low Temperature

Benzene Thermal Conversion to Nanocrystalline Indium Nitride from Sulfide at Low Temperature.

Synthesis of Carbon Nitride Nanotubes with the C3N4 Stoichiometry Via a Benzene-Thermal Process at Low Temperatureselectronic Supplementary Information (ESI) Available: XRD Patterns. See Http://Www.rsc.org/suppdata/cc/b3/b311390f/

Synthesis Of Carbon Nitride Nanotubes With The C3n4 Stoichiometry Via A Benzene-Thermal Process At Low Temperatures

Rapid thermal nitridation of thin chromium films

A Simple Route to Prepare Nanocrystalline Titanium Carbonitride

Thermodynamic Studies of the Fe-Cr-C-N System by Emf Measurements

Crystalline Carbon Nitride Film Synthesized by Ion Beam Assisted Magnetron Sputtering and Thermal Annealing in Nitrogen Gas

A novel organothermal reduction process for producing nanocrystalline Ni 2 P with a circular-shaped flake morphology

A novel organothermal reduction process for producing nanocrystalline Ni<sub>2</sub>P with a circular-shaped flake morphology

Study of Chromium Activity in the Cr-Fe-N System by Galvanic Cell Method

An Efficient Strategy for Formation of C-N Bond by Benzyl Chloride over Nano Α-Fe2o3

Synthesis of titanium nitride via hybrid nanocomposites based on mesoporous TiO2/acrylonitrile

Synthesis of Stoichiometric and Bulk CrN Through a Solid-State Ion-Exchange Reaction.

Benzene-thermal synthesis and optical properties of CdS nanocrystalline

Thermodynamic and kinetic analyses of vacuum synthesis of AlN by the alumina carbothermal reduction nitridation method