Abstract:The size- and composition-controlled synthesis of Ni-P nanospheres from nickel chloride and sodium hypophosphite has been systematically investigated by changing the conditions, such as the ratio of the starting materials, pH value, and reduction temperature. It was found that when the starting ratio of H2PO2-/Ni2+ was changed the size and chemical composition of the nanoparticles changed simultaneously. Within a suitable pH range, the phosphorus content was altered without affecting the particle size. Increasing the reduction temperature resulted in smaller Ni-P nanospheres but invariable phosphorus content. The Ni-P nanospheres were amorphous when the phosphorus content was higher than 10.0 mol %, while lower phosphor-us content led to a composite of amorphous Ni-P and face-centered cubic (fcc) Ni. During postsynthesis calcinations, amorphous Ni-P nanospheres with a low phosphorus content directly crystallized to Ni3P and fcc Ni. However, the specimens with high phosphorus content crystallized via some intermediate phases such as Ni5P, and Ni12P5. In the latter, an amorphous P-rich shell was developed simultaneously. A preliminary catalytic test of growth of carbon nanofibers on the Ni-P nanospheres has been carried out.

A novel organothermal reduction process for producing nanocrystalline Ni 2 P with a circular-shaped flake morphology

A novel organothermal reduction process for producing nanocrystalline Ni<sub>2</sub>P with a circular-shaped flake morphology

A Hydrothermal Method for Low-Temperature Growth of Nanocrystalline Pyrite Nickel Diselenide

Solution-phase synthesis of nickel phosphide single-crystalline nanowires

Size- and Structure-Controlled Synthesis and Characterization of Nickel Nanoparticles

Synthesis of iron–nickel nanoparticles via a nonaqueous organometallic route

Preparation of nanocrystalline nickel powders through hydrothermal-reduction method

Preparation of hexagonal close-packed nickel nanoparticles via a thermal decomposition approach using nickel acetate tetrahydrate as a precursor

In-situ XAFS Study on the Crystallization Mechanism of NiB Nano-Amorphous Alloy

Controlled synthesis, characterization, and crystallization of Ni-P nanospheres.

In-Situ XAFS Investigation of the Crystallization Mechanism of Ni-B Nano-Amorphous Alloy

Hydrothermal synthesis of nano nickel phosphides and investigation of their thermal stability

A Low Temperature Mechanochemical Synthesis And Characterization Of Amorphous Ni-B Ultrafine Nanoparticles

In-situ XAFS study on structures and devitrifications of Ni–B nano-amorphous alloys

Crystallization Behavior of the Ultrafine Amorphous Nickel-Phosphorus Alloy Particles

Local Structure and Catalytic Performance of Ultrafine NiB Amorphous Alloy

Structural Study of Ni-B Ultrafine Amorphous Alloy During Annealed Crystallization

A Novel Synthesis of Ni 2 P Catalysts by Reducing Nickel Sulfide at Low Temperature

Preparations,Structures and Properties of Amorphous Ni-P Alloy Catalysts

Simple, convenient, mild solvothermal route to nanocrystalline Cu3P and Ni2P

XPS Studies on a Novel Amorphous Ni–Co–W–B Alloy Powder