Abstract:Graphitic carbon nitride (g-C 3 N 4 ) and carbon nitride nanotube (CNNTs) were synthesized by the pyrolysis-assisted chemical vapor deposition (PA-CVD)—pyrolysis method. The crystal structure, surface morphology, and photoluminescence properties of these materials were influenced by the deposition temperature and the choice of metal substrate. This study provides a detailed discussion of the structural growth of CNNTs and graphitic carbon nitride. As the temperature increases to 800 °C, the quantity of amorphous nature in the carbon structures increases along with an increase in the defect states. The d-spacing of interlayers of g-C 3 N 4 and carbon nitride nanotubes (CNNTs) obtained from X-ray diffraction are 3.2 Ȧ and 3.3 Ȧ, respectively. The calculated crystallite size is about 87 nm for g-C 3 N 4, and the lattice strain is 3.14. FESEM analysis shows a clear difference in the nanotube structures, CNNTs prepared at 600 °C have linear structures with a minimum of 60 nm diameters, whereas CNNTs prepared at 800 °C show spiral, knot, and irregular structures with a minimum of 40 nm diameter. In addition, the nano-level features and interplanar spacings are confirmed by HRTEM and SAED investigations. The maximum photoluminescence intensity observed at 574 nm and 579.5 nm for g-C 3 N 4 on Cu substrate at 800 °C lies in the yellow light region. Additionally, smaller peaks were noted at higher wavelengths in the visible light spectrum. The estimated optical bandgap from the prepared samples from photoluminescence studies lies around 2.14 eV.

Characterization of well-crystallized graphitic carbon nitride nanocrystallites via a benzene-thermal route at low temperatures

Synthesis of Carbon Nitride Nanotubes with the C3N4 Stoichiometry Via a Benzene-Thermal Process at Low Temperatureselectronic Supplementary Information (ESI) Available: XRD Patterns. See Http://Www.rsc.org/suppdata/cc/b3/b311390f/

Synthesis of Carbon Nitrides with Graphite-Like or Onion-Like Lamellar Structures Via a Solvent-Free Route at Low Temperatures

Synthesis Of Carbon Nitride Nanotubes With The C3n4 Stoichiometry Via A Benzene-Thermal Process At Low Temperatures

Benzene-thermal preparation of nanocrystalline chromium nitride

Preparation of graphitic carbon nitride by electrodeposition

Low-Temperature Synthesis of Nanocrystalline Titanium Nitride via a Benzene-Thermal Route

High-Temperature High-Pressure Synchrotron X-Ray Diffraction Study Of C3n4

Structural, morphological, and photoluminescence properties of nitrogen-doped CNTs and graphitic carbon nanostructures

Crystalline Carbon Nitride Film Synthesized by Ion Beam Assisted Magnetron Sputtering and Thermal Annealing in Nitrogen Gas

A Benzene-Thermal Synthetic Route to Nanocrystalline GaN

Synthesis and characterization of single-crystalline graphitic C3N4 nanocones

Crystalline Carbon Nitride Films Prepared by Microwave Plasma Chemical Vapour Deposition

Synthesis and Thermal Decomposition of Carbon Nitride Films Prepared by Nitrogen Ion Implantation into Graphite

C3N4: Dream or reality? Solvothermal synthesis as macroscopic samples of the C3N4 graphitic form

Synthesis and characterization of polyether structure carbon nitride

New Complete Assignment of X-ray Powder Diffraction Patterns in Graphitic Carbon Nitride Using Discrete Fourier Transform and Direct Experimental Evidence.

Synthesis of Nanocrystalline Carbon Nitride Films by Glow Discharge Plasma Beam Deposition

Synthesis of C3N4+ by the Combination of Laser Ablation of Graphite and N2 Molecular Beam

Deposition of crystalline C3N4 films via microwave plasma chemical vapour deposition

Synthesis of multi-walled and bamboo-like well-crystalline CNx nanotubes with controllable nitrogen concentration (x = 0.05-1.02).