Abstract:The hot -dip 55 wt%Al-Zn-1.6 wt%Si-(0-3)wt.%Mg alloy coatings were experimentally investigated, and the solidification behaviors and hot cracking susceptibility were simulated by means of CALPHAD (CALculation of PHAse Diagrams) method. The scanning electron microscopy (SEM), electron probe micro -analyzer (EPMA) and glow discharge spectrometer method (GDS) were utilized to determine the microstructures and the distribution of elements of the Al-Zn-Mg alloy coatings with different Mg contents. It is discovered that with the increase of Mg content, the percentage of the eutectic microstructure scales up, and the surface quality of the alloy coating is improved. Meanwhile, the bending properties of Al-Zn-Mg coatings with different Mg contents still requires further improvement according to the present bending test. Subsequently, the equilibrium solidification processes of the coatings were calculated using thermodynamic approach. In general, the calculated results reflect the solidified phases and the precipitated temperatures according to theory of equilibrium solidification. However, there still exist discrepancies between the thermodynamic calculation results and the observed experimental results during the practical galvanizing process, because the cooling rates were not taken fully into consideration. Consequently, the kinetic analysis was carried out to obtain the secondary dendrite arm spacing under different cooling rates. The cracking susceptibility index (CSI) was also calculated to predict the hot workability of the Al-Zn-Mg alloy coating. In summary, the appropriate increase of the cooling rate turns out be the effective approach to benefit the microstructure and the corrosion resistance of the Al-Zn-Mg coatings in the practical galvanizing process, and the coating is not suitable for the hot stamping process.

Research on Coating Microstructure and Corrosion Behavior of Galvanized Zn-Al-Mg Coated Steel Sheet

Roles of Al and Mg on the Microstructure and Corrosion Resistance of Zn-Al-Mg Hot-Dipped Coated Steel

Corrosion Properties of Steel Sheet with Zinc-base Alloyed Coatings

Corrosion Properties of Steel Sheet with Zinc-Base Alloy Coatings

Progress in Preparation of Corrosion Resistant Zinc-magnesium Alloying Coating

The characteristics of Zn–5Al–2Mg coating on low carbon steel by two-step galvanizing method

Anticorrosive Mechanism of Vapor Deposited Mg Coating on Galvanized Steel Sheets

Corrosion behavior and mechanism of electric arc-sprayed Al-Mg coating and Zn-Al-Mg pseudo-alloy coatings

Preparation, Wear Resistance, and Corrosion Performance of Arc-Sprayed Zn, Al, and Zn-Al Coatings on Carbon Steel Substrates

Effects of Al-Mg on the Microstructure and Phase Distribution of Zn-Al-Mg Coatings

Experimental Investigation and Kinetic Analysis of Al–Zn–Mg Alloy Coating

Anti-corrosion Mechanism of Zn-Mg Alloy Coating on Steel Prepared by Vacuum Evaporation

Effects of Si Addition on Interfacial Microstructure and Corrosion Resistance of Hot-Dip Zn–Al–Mg–Si Alloy-Coated Steel

Influence mechanism of different elements and alloy phases on the corrosion resistance of Zn-Al-Mg coated steel in the atmospheric environment: A review

Study on the Alloy Coatings Properties of the New Rare Earth Yttrium Zinc Aluminum Magnesium

Effect of Dipping Time on Microstructure and Properties of Zn-1Al-2Mg Coating by Hot-Dipping Galvanizing

Effect of Mg on the Corrosion Resistance of Hot-Dip Zn-Cu-Ti Alloy

Corrosion mechanisms of Al‐alloyed hot‐dipped zinc coatings in wet supercritical carbon dioxide

Study on the formation and corrosion mechanism of black spot defects on the surface of industrial continuously hot-dip galvanized Zn-2Al-1.5Mg coating

Microstructure and Corrosion Resistance Property of a Zn-AI-Mg Alloy with Different Solidification Processes

Effects of Al contents on microstructure and properties of hot-dip Zn-Al alloy coatings on hydrogen reduced hot-rolled steel without acid pickling