Abstract:Indium tin oxide (ITO) nanofibers and ITO nanoparticles with enriched oxygen- defects were synthesized through facile electrospinning and sol-gel method. SnCl2, InCl3, and PVP (polyvinylpyrrolidone) were selected as precursors, while ethanolamine was employed as a hydrolysis controlling agent. The morphology, crystal structure, oxygen defects, and electrical performance of the ultrafine ITO nanofibers and nanoparticles were systematically characterized by transmission electron microscope (TEM), selection electron diffraction (SAED), scanning electron microscope (SEM), thermogravimetric analysis (TGA), X-ray diffraction (XRD), X-ray electron spectroscopy (XPS), and four point resistance tester. The ITO nanofibers were obtained by removal of the PVP matrix at 400 degrees C, and featured with ultrafine diameter, porous structure, and cubic phase. Furthermore, the resultant ITO nanofibers changed to oxygen. deficient nanoparticles with a high oxygen vacancy content of 38.9% at 800 degrees C The doping of Sn4+ ions into the In2O3 lattices leads to the expansion of the lattice and thus the increase of crystal plane spacing at elevated temperatures. When the temperature increased from 400 to 800 degrees C, the size of ITO nanoparticles grown from 32 to 44 nm. Meanwhile, the lattice strain (epsilon(0)) decreased from 1.943 x 10(-3) to 1.422 x 10(-3) and the strain-induced lattice relaxation decreased accordingly. No phase change from cubic structure to hexagonal structure was observed. Additionally, calcination at elevated temperature could hamper the (111) growth and thus cause the increase in the ratio of I-(400)/I-(222) in In2O3 that is proportional to the electrical conductivity of ITO. The maximized electrical conductivity of ITO nanoparticles was obtained upon a calcination temperature of 800 degrees C.

Synthesis of 3D Ordered Macroporous Indium Tin Oxide Using Polymer Colloidal Crystal Template

Gas Phase Fabrication of Morphology-Controlled ITO Nanoparticles and Their Assembled Conductive Films.

Effect of Different Thermo-Treatment at Relatively Low Temperatures on the Properties of Indium‑tin-Oxide Thin Films

Fabrication Of Indium Tin Oxide Nanostructures By Electrospinning And Their Electrical Conductivity

Optimization Preparation of Indium Tin Oxide Nanoparticles via Microemulsion Method Using Orthogonal Experiment

Preparation and characterization of hollow spherical indium tin oxide with micro size by template assisted hydrothermal method

Deposition of Transparent Conductive Mesoporous Indium Tin Oxide Thin Films by A Dip Coating Process

Shape-Controlled Synthesis of Porous Screw-Cap-Like Indium Tin Oxide and Its Application for Gas Sensing

Template synthesis of tin-doped indium oxide (ITO)/polymer and the corresponding carbon composite hollow colloids

Dye-Sensitized Nanostructured Crystalline Mesoporous Tin-doped Indium Oxide Films with Tunable Thickness for Photoelectrochemical Applications

Electrochemical synthesis of a microporous conductive polymer based on a metal-organic framework thin film.

Thin Indium-Tin-Oxide Film Produced Through Sol–Gel Method with Its Morphological and Electrical Properties

Mesoporous Indium Oxide Synthesized Via a Nanocasting Route

A Sol–gel Method to Synthesize Indium Tin Oxide Nanoparticles

3D Ordered Macro–mesoporous Indium Doped Al2O3

Preparation of a Porous ITO Electrode

Amorphous Indium Tin Oxide Films Deposited on Flexible Substrates by Facing Target Sputtering at Room Temperature

Porous Crystalline Iron Oxide Thin Films Templated by Mesoporous Silica

General Synthesis of 3D Ordered Macro-/Mesoporous Materials by Templating Mesoporous Silica Confined in Opals

Preparation of Nano-Powders of ITO

Synthesis of Indium Tin Oxide Nanotubes Using 2-Methoxyethanol As Solvent Via Simple Template Method