Abstract:Mixed IrO2–SiO2 oxide films were prepared on titanium substrate by the thermo-decomposition of hexachloroiridate (H2IrCl6) and tetraethoxysilane (TEOS) mixed precursors in organic solvents. The solution chemistry and thermal decomposition kinetics of the mixed precursors were investigated by ultra violet/visible (UV/vis) spectroscopy and thermogravimetry (TGA) and differential thermal analysis (DTA), respectively. The physiochemical characterization of the resulting materials was conducted by X-ray diffraction (XRD), scanning electron microscopy (SEM) and electrochemical measurements. It is shown from the UV/vis spectra that the electronic absorption intensity of IrCl62− complexes in the precursors decreases in the presence of TEOS, indicating the interaction between these two components. Thermal analysis shows the decomposition reaction of H2IrCl6 is inhibited by TEOS in the low temperature range, but the further oxidation reaction at high temperatures of formed intermediates is independent of the presence of silane component. Physical measurements show a restriction effect of silica on the crystallization and crystal growth processes of IrO2, leading to the formation of finer oxide particles and the porous morphology of the binary oxide films. The porous composite films exhibit high apparent electrocatalytic activity toward the oxygen evolution reaction. In addition, the long-term stability of Ti-supported IrO2 electrodes is found to apparently improve with appropriate amount of SiO2 incorporation, as tested under galvanostatic electrolysis.

Porous Crystalline Iron Oxide Thin Films Templated by Mesoporous Silica

P-type Tin–indium Oxide Films Prepared by Thermal Oxidation of Metallic InSn Alloy Films

Influence of Iron Dopant on Crystallization and Photo-Induced Hydrophilicity of TiO2 Thin Films

Gas Phase Fabrication of Morphology-Controlled ITO Nanoparticles and Their Assembled Conductive Films.

Oriented Zeolite Mfi Monolayer Films on Metal Substrates by in Situ Crystallization

Synthesis of Tio 2 Meso-Structured Thin Films

Formation Mechanism of Porous Single-Crystal Cr(2)O(3) and Co(3)O(4) Templated by Mesoporous Silica

Structural and Optical Characteristics of TiO2 Nanoparticles-Containing Mesoporous Silica (SBA-15) Thin Films

Preparation Of Nanocrystalline Titania Mesoporous Films By Template Assembled Method

Seed-Mediated Hydrothermal Synthesis and Photoelectrochemical Properties of Hematite Thin Films

Ordered mesoporous silica nanoparticles with and without embedded iron oxide nanoparticles: structure evolution during synthesis

Preparation Of Three-Dimensional Chromium Oxide Porous Single Crystals Templated By Sba-15

Hydrothermal Preparation and Characterization of Nanocrystalline Porous Tin Dioxide Thin Films

Highly Crystallized Mesoporous Tio2 Films and Their Applications in Dye Sensitized Solar Cells

Study on the Preparation and Properties of Colored Iron Oxide Thin Films

Synthesis of Transition-Metal-Oxides Meso-Structured Thin Films

Synthesis of Continuous Mesoporous Silica Thin Films with Three-Dimensional Accessible Pore Structures

Preparation of Tin Modified Silica Mesoporous Film

Structure and Characteristics of the BiFeO3 Fabricated by the Sol-Gel Technique

IrO2–SiO2 Binary Oxide Films: Preparation, Physiochemical Characterization and Their Electrochemical Properties

Achievement of thick mesoporous TiO2 crystalline films by one-step dip-coating approach