Catalytic Performance and Reaction Pathways of Cu/SiO 2 and ZnO/SiO 2 for Dehydrogenation of Ethanol to Acetaldehyde
Masahiro Ohira,Huimin Liu,Dehua He,Yoshiya Hirata,Makoto Sano,Toshimitsu Suzuki,Takanori Miyake
DOI: https://doi.org/10.1627/jpi.61.205
2018-01-01
Journal of the Japan Petroleum Institute
Abstract:Vapor-phase dehydrogenation of ethanol to acetaldehyde was studied using Cu/SiO2 and ZnO/SiO2 catalysts prepared by the conventional impregnation method. Catalysts were characterized by XRD, nitrogen adsorption-desorption analysis, XPS, N2O-pulse method, CO2-TPD and C2H5OH-TPD. Use of copper ammonium complex for the preparation of Cu/SiO2 catalysts formed Cu particles on SiO2 too small for detection by XRD. The prepared Cu/SiO2 catalyst had high and selective dehydrogenation activity of ethanol to acetaldehyde. However, Cu/SiO2 catalyst was less stable at 350 degrees C due to sintering of Cu. Interestingly, a metal oxide catalyst, ZnO/SiO2, had fairly high and fully selective activity for dehydrogenation of ethanol to acetaldehyde. Furthermore, no changes in the activity and selectivity were observed for at least 6 h at 350 degrees C. The reaction pathways on the metal catalyst, Cu/SiO2, and the oxide catalyst, ZnO/SiO2, were studied by C2H5OH-TPD. Evolution of H-2 was observed from ethanol contacted with Cu/SiO(2 )catalyst at 50 degrees C, suggesting dehydrogenation at this temperature. Desorption of acetaldehyde was observed above 200 degrees C. On the other hand, simultaneous desorption of H-2 and acetaldehyde occurred on ZnO/SiO2 catalyst above 240 degrees C, suggesting that the rate determining step is the dissociative adsorption of ethanol at this temperature. Thus, the reaction pathways were very different for the metal catalyst and the oxide catalyst.