Abstract:A series of K-ZrO2/Cu/Al2O3 catalysts (KZC(T)A (T= 600-900 degrees C)) were prepared by a sequential impregnation method and investigated for the direct synthesis of ethanol and isobutanol from syngas. The calcination temperature for C(T)A (T= 600-900 degrees C) preparation had considerable effect on the structure and catalytic performance of KZCTA catalysts. By increasing the calcination temperature from 600 to 900 degrees C, the CO conversion was promoted obviously from 20.3 to 53.0%. When the calcination temperature was lower, KZC(700)A catalyst showed high isobutanol selectivity of 17.7 wt%, while only a small amount of isobutanol was obtained in the reference catalysts of KZA and KC(700)A without Cu or Zr as promoters. The coexistence of Cu and Zr in the catalyst was required for isobutanol formation. Furthermore, the Cu-ZrO2 interface amounts increased firstly with the increase of calcination temperature and then decreased at over-higher calcination temperature because of the aggregation of ZrO2. The isobutanol selectivity changed with the Cu-ZrO2 interface amounts in catalyst, suggesting that the Cu-ZrO2 interfaces were responsible for isobutanol preferable synthesis directly from syngas. In addition, ethanol selectivity increased clearly up to 36.3 wt% when the higher calcination temperature 900 degrees C was employed for catalyst preparation. In comparison with the KZC(900)A catalyst, the catalyst of KC(900)A prepared without Zr as promoter exhibited excellent catalytic performance for the ethanol synthesis (33.5 wt%). It revealed that Zr cannot contribute to ethanol formation, and the newly formed CuAlO2 phase under higher calcination temperature in the catalysts possibly favored ethanol formation. As confirmed by XRD, Raman spectroscopy and H-2-TPR, the CuAlO2 phase emerged and its amount increased with the increase of calcination temperature for catalyst preparation. A good linear relationship was found between ethanol selectivity and the amount of CuAlO2, proving that the CuAlO2 phase acted as efficient active sites for ethanol preferable synthesis directly from syngas.

Effect of the ZrO 2 Crystal Phase on Performance over a CuCeZrO Catalyst for Dehydrogenative Condensation of Ethanol to Ethyl Acetate

Effect of the ZrO2 Crystal Phase on Performance over a CuCeZrO Catalyst for Dehydrogenative Condensation of Ethanol to Ethyl Acetate

Strong Cu/ZnO Interfacial Interaction Induced by ZrO2 Promoter Suppressing the Ethanol Formation in Industrial Methanol Synthesis

Ce doping promote the selective conversion of ethanol to ethyl acetate via the dehydrogenation-condensation over CuCeZr catalyst

Effect of Preparation Method on ZrO2-Based Catalysts Performance for Isobutanol Synthesis from Syngas

Zr 0.1 /(Fe Ce) as highly efficient catalyst for direct synthesis of diethyl carbonate from ethanol with fermentation tail gas as CO 2 raw material

Structural Evolution and Catalytic Properties of Nanostructured Cu/Zro2 Catalysts Prepared by Oxalate Gel-Coprecipitation Technique

Investigation of the Structural Evolution and Catalytic Performance of the Cuznal Catalysts in the Hydrogenation of Dimethyl Oxalate to Ethylene Glycol

The effect of CuO crystallite size on the structure and performance of CuZnAl catalyst for mixed alcohols synthesis from syngas

Catalytic Performance and Reaction Pathways of Cu/SiO 2 and ZnO/SiO 2 for Dehydrogenation of Ethanol to Acetaldehyde

Cu/ZnO/Al2O3 Catalyst Modulated by Zirconia with Enhanced Performance in CO2 Hydrogenation to Methanol

Low-Temperature Dehydration of Ethanol to Ethylene over Cu–Zeolite Catalysts Synthesized from Cu–Tetraethylenepentamine

Effects of Calcination Temperature on Structure-Activity of K-ZrO2/Cu/Al2O3 Catalysts for Ethanol and Isobutanol Synthesis from CO Hydrogenation

Complete liquid-phase preparation and characterization of Cu-Zn-Al-Zr slurry catalysts for synthesis of dimethyl ether

The Effects of the Crystalline Phase of Zirconia on C–O Activation and C–C Coupling in Converting Syngas into Aromatics

Influences of preparation methods of ZrO2 support and treatment conditions of Cu/ZrO2 catalysts on synthesis of methanol via CO hydrogenation

Synergistic Performance Between Oxidizability and Acidity/texture Properties for 1,2-Dichloroethane Oxidation over (ce,cr)xo2/zeolite Catalysts

Synthesis of Cu-Ce0.8Zr0.2O2 catalyst by ball milling for CO2 reforming of ethanol

Solvothermal Preparation of CuO-ZnO-ZrO2 Catalysts for Methanol Synthesis Via CO2 Hydrogenation

Zn-Zr-Al Oxides Derived from Hydrotalcite Precursors for Ethanol Conversion to Diethyl Carbonate

A CuZn-BTC derived stable Cu/ZnO@SiO2 catalyst for ethanol dehydrogenation