Abstract:This paper describes the effect of hot extrusion on the microstructure and mechanical properties of electromagnetic continuous cast (EMC) AZ31 alloy. The microstructure, mechanical properties and fracture surfaces of AZ31 alloy before and after extrusion were investigated. The results demonstrate that extrusion processing gives rise to a strong basal texture. The grains are significantly refined and the average grain size of localized fine grain area is 2μm. Compared with EMC ingots, as-extruded specimens have much finer grain size and more uniform microstructure, and the second phase ( Mg 17 Al 12 ) becomes smaller and distributes more uniformly. The mechanical properties of the deformed AZ31 were improved after hot-extrusion. When the extrusion ratio was 10, the yield strength, ultimate tensile strength and reduction in cross-sectional area of as-extruded AZ31 alloy were 248MPa, 306MPa and 28.44%, which were respectively enhanced by 78.4%, 41% and 45.25%, compared with those of as-cast samples. With the increase of extrusion ratio, the grain refining effect was more significant and the microstructure was more uniform. The yield strength, ultimate tensile strength and reduction in cross-sectional area increased obviously with increasing the extrusion ratio. The observation on fracture surfaces demonstrates that the fracture mode changes from ductile-brittle fracture to ductile fracture after extrusion.

Effect Of Eche Forming On The Microstructure And Mechanical Properties Of Az31 Magnesium Alloy

Microstructure and Mechanical Properties of Magnesium Alloy AZ31 Processed by Compound Channel Extrusion

Effect of Equal Channel Angular Extrusion on the Microstructure and Mechanical Properties of AZ31 Magnesium Alloy

Deformation Behaviors of AZ31 Magnesium Alloy by Equal Channel Angular Extrusion

Effects of Die Angle on Microstructures and Mechanical Properties of AZ31 Magnesium Alloy Processed by Equal Channel Angular Pressing

Microstructural evolution and mechanical properties of AZ31 Mg alloy fabricated by a novel bifurcation-equal channel angular pressing

Three-Dimensional Numerical Simulation and Experimental Study of Severe Plastic Deformation of Az31 Magnesium Alloy

The Microstructure and Mechanical Properties of AZ31 Mg Alloy Processed by Two-Step Equal Channel Angular Extrusion

Microstructure Evolution and Mechanical Properties of AZ 31 Mg Alloy Processed by Equal Channel Angular Extrusion

Microstructure and mechanical properties of AZ31 Mg alloy processed by two-step equal channel angular extrusion

Microstructure and Mechanical Properties of AZ31 Mg Alloy Processed by Equal Channel Angular Pressing (ECAP)

Effects of Direct Extrusion Process on Microstructure, Texture Evolution and Yield Strength of Magnesium Alloy Az31

Change-Channel Angular Extrusion of Magnesium Alloy Az31

Effect of Extrusion-Sheer on the Microstructure and Mechanical Properties of Magnesium Alloy AZ31

Study on the Effect of the ECAP Deformation on the Organization and Properties of the Extruded Mg-Sn-Al Alloys

The effect of texture on the mechanical properties of AZ31 MG alloy by equal channel angular extrusion

Mechanical Properties and Microstructure of AZ31 Mg Alloy Processed by Two-Step Equal Channel Angular Extrusion

Effect of Hot Extrusion on Microstructure and Mechanical Properties of Electromagnetic Continuous Cast Az31 Magnesium Alloy

An Electron Back-Scattered Diffraction Study on the Microstructure Evolution of AZ31 Mg Alloy During Equal Channel Angular Extrusion

Microstructure Evolution and Mechanical Properties of AZ80 Mg Alloy during Annular Channel Angular Extrusion Process and Heat Treatment

Effect of Extrusion Deformation on Microstructures and Properties of AZ31 Magnesium Alloy