Abstract:Microstructure evolution and mechanical properties of AZ80 Mg alloy during annular channel angular extrusion (350 °C) and heat treatment with varying parameters were investigated, respectively. The results showed that dynamic recrystallization of Mg grains was developed and the dendritic eutectic β-Mg17Al12 phases formed during the solidification were broken into small β-phase particles after hot extrusion. Moreover, a weak texture with two dominant peaks formed owing to the significant grain refinement and the enhanced activation of pyramidal slip at relative high temperature. The tension tests showed that both the yield strength and ultimate tensile strength of the extruded alloy were dramatically improved owing to the joint strengthening effect of fine grain and β-phase particles as compared with the homogenized sample. The solution treatment achieved the good plasticity of the alloy resulting from the dissolution of β-phases and the development of more equiaxed grains, while the direct-aging process led to poor alloy elongation as a result of residual eutectic β-phases. After solution and aging treatment, simultaneous bonding strength and plasticity of the alloy were achieved, as a consequence of dissolution of coarse eutectic β-phases and heterogeneous precipitation of a large quantity of newly formed β-phases with both the morphologies of continuous and discontinuous precipitates.

Microstructure and Mechanical Properties of Magnesium Alloy AZ31 Processed by Compound Channel Extrusion

Change-Channel Angular Extrusion of Magnesium Alloy Az31

Microstructure and mechanical properties of AZ31 Mg alloy processed by two-step equal channel angular extrusion

The Microstructure and Mechanical Properties of AZ31 Mg Alloy Processed by Two-Step Equal Channel Angular Extrusion

Microstructure Evolution and Mechanical Properties of AZ 31 Mg Alloy Processed by Equal Channel Angular Extrusion

Microstructure and Properties of Magnesium Alloy Processed by a New Severe Plastic Deformation Method

Mechanical Properties and Microstructure of AZ31 Mg Alloy Processed by Two-Step Equal Channel Angular Extrusion

Effect Of Eche Forming On The Microstructure And Mechanical Properties Of Az31 Magnesium Alloy

Effect of Equal Channel Angular Extrusion on the Microstructure and Mechanical Properties of AZ31 Magnesium Alloy

Microstructure and Mechanical Properties of AZ31 Mg Alloy Produced by a New Compound Extrusion Technique

Deformation Behaviors of AZ31 Magnesium Alloy by Equal Channel Angular Extrusion

Microstructural evolution and mechanical properties of AZ31 Mg alloy fabricated by a novel bifurcation-equal channel angular pressing

Microstructure and Mechanical Properties of AZ31 Mg Alloy Fabricated by Pre-compression and Frustum Shearing Extrusion

Microstructure Evolution and Mechanical Properties of AZ80 Mg Alloy during Annular Channel Angular Extrusion Process and Heat Treatment

Improving the Microstructure and Mechanical Properties of Magnesium-Alloy Sheets with a New Extrusion Method

Change Channel Angular Extrusion Process of AZ31 Magnesium Alloy

Microstructural Analysis and Mechanical Properties of AZ31 Magnesium Alloy Prepared by Alternate Extrusion (AE)

Microstructure Evolution of AZ31 Mg Alloy During Equal Channel Angular Extrusion

A Study of Microstructure Evolution for Mg Alloy Subjecting to Multi-Pass Equal Channel Angular Extrusion

Microstructure and Mechanical Properties of AZ31 Mg Alloy Processed by Equal Channel Angular Pressing (ECAP)

Effects of Die Angle on Microstructures and Mechanical Properties of AZ31 Magnesium Alloy Processed by Equal Channel Angular Pressing