Microstructure and electrochemical characterization of solid oxide fuel cells fabricated by co-tape casting
Xiaoliang Zhou,Kening Sun,Jie Gao,Shiru Le,Naiqing Zhang,Peng Wang
DOI: https://doi.org/10.1016/j.jpowsour.2009.02.008
IF: 9.2
2009-01-01
Journal of Power Sources
Abstract:A co-tape casting technique was applied to fabricate electrolyte/anode for solid oxide fuel cells. YSZ and NiO–YSZ powders are raw materials for electrolyte and anode, respectively. Through adjusting the Polyvinyl Butyral (PVB) amount in slurry, the co-sintering temperature for electrolyte/anode could be dropped. After being co-sintered at 1400°C for 5h, the half-cells with dense electrolytes and large three phase boundaries were obtained. The improved unit cell exhibited a maximum power density of 589mWcm−2 at 800°C. At the voltage of 0.7V, the current densities of the cell reached 667mAcm−2. When the electrolyte and the anode were cast within one step and sintered together at 1250°C for 5h and the thickness of electrolyte was controlled exactly at 20μm, the open-circuit voltage (OCV) of the cell could reach 1.11V at 800°C and the maximum power densities were 739, 950 and 1222mWcm−2 at 750, 800 and 850°C, respectively, with H2 as the fuel under a flow rate of 50sccm and the cathode exposed to the stationary air. Under the voltage of 0.7V, the current densities of cell were 875, 1126 and 1501mAcm−2, respectively. These are attributed to the large anode three phase boundaries and uniform electrolyte obtained under the lower sintering temperature. The electrochemical characteristics of the cells were investigated and discussed.