Wu Gang,Wang Ying-Jun,Chen Xiao-Feng,Ye Jian-Dong,Wei Kun,Leon Betty
DOI: https://doi.org/10.3321/j.issn:0251-0790.2008.08.030
2008-01-01
Abstract:Surface physical and chemical properties have very important impacts on biocompatibility of biopolymers. In this article, a 193nm excimer laser was used for the PET surface modification. The PET film was irradiated in a vacuum chamber filled with controlled ammonia flux. Surface roughness measurement, water contact angle, FTIR/ATR, XPS and Tof-SIMS were used to characterize the modified PET film surface. Water contact angle decreasing indicates that the chemical composition changed after laser Irradiation in ammonia and no significant surface roughness was observed. The character amino group vibration absorption hands were displayed in FTIR/ATR spectrum at 3352 and 1613 cm respectively. XPS binding energies of C-15 at 285.5 eV and N-15 at 398. 9 eV verified the C-N bond's formation on the PET film surface. Fragment tons mapping in Tof-SIMS also shows that the proofs of amine molecule fragments could be extracted from the laser irradiated PET surface. All the results prove that the excimer laser can be Used as a useful tool for the biopolymer surface modification and chemical patterning.
What problem does this paper attempt to address?