Anisotropy of the Optimally-Doped Iron Pnictide Superconductor Ba(Fe0.926Co0.074)2As2
M. A. Tanatar,N. Ni,C. Martin,R. T. Gordon,H. Kim,V. G. Kogan,G. D. Samolyuk,S. L. Bud'ko,P. C. Canfield,R. Prozorov
DOI: https://doi.org/10.1103/PhysRevB.79.094507
2008-12-30
Abstract:Anisotropies of electrical resistivity, upper critical field, London penetration depth and critical currents have been measured in single crystals of the optimally doped iron pnictide superconductor Ba(Fe$_{1-x}$Co$_x$)$_2$As$_2$, $x$=0.074 and $T_c \sim$23 K. The normal state resistivity anisotropy was obtained by employing both the Montgomery technique and direct measurements on samples cut along principal crystallographic directions. The ratio $\gamma_{\rho} = \rho_c /\rho_a$ is about 4$\pm$1 just above $T_c$ and becomes half of that at room temperature. The anisotropy of the upper critical field, $\gamma_{H} = H_{c2,ab} /H_{c2,c} $, as determined from specific heat measurements close to $T_c$, is in the range of 2.1 to 2.6, depending on the criterion used. A comparable low anisotropy of the London penetration depth, $\gamma_{\lambda}=\lambda_{c}/\lambda_{ab}$, was recorded from TDR measurements and found to persist deep into the superconducting state. An anisotropy of comparable magnitude was also found in the critical currents, $\gamma_j=j_{c,ab}/j_{c,c}$, as determined from both direct transport measurements ($\sim$1.5) and from the analysis of the magnetization data ($\sim$3). Overall, our results show that iron pnictide superconductors manifest anisotropies consistent with essentially three-dimensional intermetallic compound and bear little resemblance to cuprates.
Superconductivity,Strongly Correlated Electrons