Structure and Performance of TiC-containing Diamond-like Carbon Nanocomposite Coatings Deposited by Rectangular Cathodic Arc Ion-plating

Guosheng Xie,Zhimin Yin,Hui Ding,Xiaohong Li,Bing Yang

DOI: https://doi.org/10.1007/s11595-009-3383-7

2009-01-01

Abstract:TiC-containing diamond-like carbon (TiC-DLC) nanocomposite coatings were deposited by a rectangular cathodic arc ion-plating system using C2H2 as reacting gas. Raman spectros-copy and transmission electron microscopy analysis show that with increasing flow rate of C2H2, the structure of nanocomposite coatings changes from TiC nanograin-containing to graphite nanograin-containing DLC. The hardness measurements show that the hardness decreases from 28 GPa to 18 GPa with increasing C2H2 flow rate. The scratch test show that a high critical load (>40 N) was obtained and exhibited a good adhesion between the coating and the substrate. Wear experiment shows that the friction coefficient of TiC-DLC nanocomposite coatings decreases with increasing C2H2. A low friction coefficient of 0.07 was obtained at 480 sccm C2H2.