Abstract:Asymmetric rolling is a high-tech method based on the principles of severe plastic deformation. In the present paper, it is shown that Cu-0.8Cr-0.1Zr alloy is highly strengthened during asymmetric rolling due to structure refinement to an ultrafine-grained state. For example, in only one pass, at the accumulated strain 0.94 ± 0.20, the strength increases from 265 to 425 MPa. During the deformation process, the structure becomes refined, with the average size of fragments reaching 235 ± 90 nm. Structure heterogeneity is also observed in the cross section of a sample, which is associated with different rotation speeds of the rolls. The shape of grains in the central zone of samples corresponds to the state after conventional symmetric rolling. However, in the zone adjacent to the roll rotating at a higher speed, mechanical texture of grains is similar to that after shear. Subsequent aging of Cu-0.8Cr-0.1Zr alloy at 450°C makes it possible to achieve the ultimate strength 560 MPa and electrical conductivity 82% IACS, which exceeds the characteristics of the strengthened steel by 10–15%. The analysis of contributions to strengthening during asymmetric rolling reveals that the main contribution comes from the refinement of the grain structure to an ultrafine-grained state, which amounts to 58%. The fractions of the dislocation and dispersion contributions comprise 15 and 20%, respectively. Compared to conventional rolling, as well as other deformation methods that provide the same level of accumulated strain and strengthening in one cycle, such as equal channel angular pressing-conform, asymmetric rolling is the most promising due to its simpler process scheme.

Effect of Rolling Deformation on the Structure of Bulk Zr60cu30al10 Amorphous Alloy

Structure Evolution of Bulk Zr60Cu20Pd10Al10 Amorphous Alloy During Rolling Deformation

Influence of rolling on the precipitation of icosahedral quasicrystalline phase in Zr-Al-Ni-Cu-Ag amorphous alloy

Effect of cold rolling on microstructure and mechanical properties of pure Zr

Recrystallization Behavior and Mechanical Properties of Az31b Alloy During the Hot-Rolling Process

Effect of Rolling on the Microstructure and Mechanical Property of Zr52.5Cu17.9Ni14.6Al10Ti5 Bulk Metallic Glass

Crystallization Behavior of Zr55Al10Cu30Ni5 Bulk Metallic Glass Rolled at Room Temperature

Effect of Rolling Deformation on the Microstructure of Bulk Cu60Zr20Ti20 Metallic Glass and Its Crystallization

Nanocrystallization of Pure Zr Via Room Temperature Rolling Deformation

Revealing the Microstructure Evolution Mechanism and Mechanical Responses of a Novel Al–Zn–Mg–Cu Alloy by Hot Deformation Process

Microstructure evolution behavior and mechanical mechanisms in a near α-Zr alloy by cold rolling

Phase Transition in the Zr60Al15Ni25 Bulk Metallic Glass Subjected to Rolling at Room Temperature

Microstructure and mechanical property of Zr 65 Al 7.5 Ni 10 Cu 12.5 Ag 5 bulk metallic glass subjected to rolling

Effect of Asymmetric Rolling on the Structure and Properties of Cu-Cr-Zr Alloys

Effect of strain rate on microstructure evolutions and mechanical properties of cryorolled Zr upon annealing

Microstructural Evolution and Mechanical Properties in Zr705 During the Rolling Process

Effect of cryogenic rolling on the microstructure and texture of CuCrZr alloy

Rolling-Induced Microstructure Change in Zr65al7.5ni10cu12.5ag5 Bulk Metallic Glass

Effect of Deformation on Precipitation and the Microstructure Evolution during Multistep Thermomechanical Processing of Al-Zn-Mg-Cu Alloy

Evolution of Shear Bands in the Structure of a Zirconium-Based Amorphous Alloy during Rolling at Different Temperatures

Effects of Rolling Deformation on Precipitation Behavior and Mechanical Properties of Al–Zn–Mg–Cu Alloy