Abstract:The effect of hot rolling with different rolling deformations on the microstructure evolution and improvement of mechanical properties of the novel Al-Zn-Mg-Cu alloy are investigated via optical microscope (OM), scanning electron microscope (SEM), electron backscattered diffusion (EBSD) and transmission electron microscope (TEM). The findings showed that the equiaxed grains with low dislocation density gradually elongate to become fibrous with high dislocation density as hot rolling deformation growing, and the dynamic dissolution of precipitations occurs at the grain boundaries of small dynamic recrystallization (DRX) grains. Dislocation entanglement is formed when a high density of dislocation is clearly visible following various rolling deformations. Dislocation cells could evolve into sub-grains, and ultimately become recrystallized grains as a result of continuous energy absorption. The percentage of low angle grain boundaries (LAGBs) with varying rolling deformation increases swiftly then declines slightly which linked to more deformed grains and sub-grains, as well as less recrystallized grains. High angle grain boundaries (HAGBs), however, show the opposite pattern. Ultimate tensile strength (UTS) and yield strength (YS) of the alloys reach peaks at deformation of 90% (UTS: 620.0 MPa, YS: 583.7 MPa). Which is predominantly attributed to the texture enhancement, grain refinement, and pinning effect of Al3(Sc, Zr, Ti) particles of L12 structure on the grain boundaries and dislocations.

Structure Evolution of Bulk Zr60Cu20Pd10Al10 Amorphous Alloy During Rolling Deformation

Effect of Rolling Deformation on the Structure of Bulk Zr60cu30al10 Amorphous Alloy

Effect of Rolling on the Microstructure and Mechanical Property of Zr52.5Cu17.9Ni14.6Al10Ti5 Bulk Metallic Glass

Microstructure and mechanical property of Zr 65 Al 7.5 Ni 10 Cu 12.5 Ag 5 bulk metallic glass subjected to rolling

Phase Transition in the Zr60Al15Ni25 Bulk Metallic Glass Subjected to Rolling at Room Temperature

Microstructural evolution during annealing and rolling Zr52.5Cu17.9Ni14.6Al10Ti5 bulk metallic glass

Rolling-Induced Microstructure Change in Zr65al7.5ni10cu12.5ag5 Bulk Metallic Glass

Crystallization Behavior of Zr55Al10Cu30Ni5 Bulk Metallic Glass Rolled at Room Temperature

Influence of rolling on the precipitation of icosahedral quasicrystalline phase in Zr-Al-Ni-Cu-Ag amorphous alloy

Effect of Rolling Deformation on the Microstructure of Bulk Cu60Zr20Ti20 Metallic Glass and Its Crystallization

Deformation-strengthening During Rolling Cu60Zr20Ti20 Bulk Metallic Glass

Effect of cold rolling on microstructure and mechanical properties of pure Zr

Microstructural Evolution and Mechanical Properties in Zr705 During the Rolling Process

Effect of Cold Rolling on Microstructure and Mechanical Property of a Novel (fe50mn30co10cr10)97c2mo1 High Entropy Alloy

Microstructure and Microhardness Evolutions of Cu47.5zr47.5al5 Bulk Metallic Glass Processed by Rolling

Evolution of Shear Bands in the Structure of a Zirconium-Based Amorphous Alloy during Rolling at Different Temperatures

Microstructure evolution behavior and mechanical mechanisms in a near α-Zr alloy by cold rolling

Microstructure Evolution in Bulk Nanostructured Copper During Repeated Cold Rolling

Revealing the Microstructure Evolution Mechanism and Mechanical Responses of a Novel Al–Zn–Mg–Cu Alloy by Hot Deformation Process

Nanocrystallization of Pure Zr Via Room Temperature Rolling Deformation

Free Volume Evolution of Pre-Annealed Zr55al10ni5cu30 Bulk Metallic Glass During Rolling