Abstract:Catalytic ammonia borane (AB) hydrolysis using supported Ni catalysts is a cost-effective way for H 2 production. However, constructing highly active Ni catalysts is still challenging due to the low intrinsic activity and easy aggregation of Ni particles at high Ni content. In this study, Ni particles in SBA-15 ( mi -Ni@SBA-15) were prepared using the template-assisted melt infiltration method. For comparison, Ni catalysts supported on SBA-15 were also prepared using conventional impregnation ( imp -Ni/SBA-15-NT) and melt infiltration method ( mi - Ni/SBA-15-NT). The catalysts were fully characterized and catalytic AB hydrolysis was carried out on the catalysts. The results showed that for imp - Ni/SBA-15-NT and mi -Ni/SBA-15-NT large Ni agglomerates were obviously observed and the mesopores of SBA-15 were partially blocked due to the formation of rodlike Ni particles. In contrast, for mi -Ni@SBA-15 the combination of the steric effect of template and tunable mesopore size of SBA-15 enables SBA-15 to effectively confine the Ni particles in its mesopores and regulate the particle size of Ni respectively. Increasing Ni content from 7.7 to 24.5 wt% only led to denser Ni particles in SBA-15 without marked growth of Ni particles for mi -Ni@SBA-15. The well-dispersed Ni particles on mi -Ni@SBA-15 with Ni content of 24.5 wt% enriched the active sites on the catalyst surface , thus leading to high catalytic activity for AB hydrolysis with a TOF of 37.8 mol H2 mol Ni −1 min −1 , which was at least 3.9 times higher than those of other tested catalysts. A comparison of the normalized catalytic activities by exposed Ni sites of catalysts with varied Ni particle sizes suggested that Ni sites on small Ni particles are more active than those on large ones. This work highlighted that mi -Ni@SBA-15 prepared using the template-assisted melt infiltration method are highly active catalysts for H 2 production from AB hydrolysis.

Preparation of Silica Sol-Supported NiB Nanoclusters and Their Catalytic Hydrogenation Performance

Sol-Gel Preparation, Characterization and Hydrogenation Property of Silica Supported Ni Catalyst

Liquid-Phase Hydrogenation of Nitrobenzene over Ag-Ni Bimetallic Catalysts Prepared by Adsorption Phase Synthesis

Preparation and Characterization of Bulk and Supported NiB Amorphous Alloy Catalysts with Different Particle Sizes

Mesoporous silica-supported NiB amorphous alloy catalysts for selective hydrogenation of 2-ethylanthraquinone

Synthesis of Mesoporous Silica-Supported NiCo Bimetallic Nanocatalysts and Their Enhanced Catalytic Hydrogenation Performance

Self-assembly of mesoporous Ni–B amorphous alloy catalysts

Hydrogenation of Nitrobenzene to Aniline over Silica Gel Supported Nickel Catalysts

Size-tunable Ni particles confined in the ordered mesoporous silica for catalytic H 2 production from ammonia borane hydrolysis

Formation Combined with Intercalation of Ni and Its Alloy Nanoparticles within Mesoporous Silica for Robust Catalytic Reactions

The Crystallization Process and the Hydrogenation Activity of Ni-P/SiO2 Catalyst

NiCuBimetallic Nanoparticles on Silica Support forCatalytic Hydrolysis of Ammonia Borane: Composition-Dependent Activityand Support Size Effect

Highly Dispersed Nickel Particles Encapsulated in Multi‐hollow Silicalite‐1 Single Crystal Nanoboxes: Effects of Siliceous Deposits and Phosphorous Species on the Catalytic Performances

Highly Dispersed Nickel-Containing Mesoporous Silica With Superior Stability In Carbon Dioxide Reforming Of Methane: The Effect Of Anchoring

Highly Dispersed Ni Nanoparticles Encapsulated in Hollow Mesoporous Silica Spheres As an Efficient Catalyst for Quinoline Hydrogenation

NiCu Bimetallic Nanoparticles on Silica Support for Catalytic Hydrolysis of Ammonia Borane: Composition-Dependent Activity and Support Size Effect

Preparation and characterization of nickel based catalysts on silica, alumina and titania obtained by sol–gel method

Two-Step, Oxygen-Free Conversion of Methane over Supported NiB Amorphous Alloy Catalysts

Ordered Mesoporous Ni Nanowires with Enhanced Hydrogenation Activity Prepared by Electroless Plating on Functionalized SBA-15

Enhanced and stabilized hydrogen production from methanol by ultrasmall Ni nanoclusters immobilized on defect-rich h-BN nanosheets

Solid-State Surface-Anchoring Strategy to Prepare Anti-Sintering Supported Metal Cluster Catalysts