In-situ TEM study on the precipitation behavior of an Al-Mn-Mg-Sc-Zr alloy formed by SLM
Wenhao Li,Pucun Bai,Xiaoming Cui,Xueping Zhao,Shaobo Liang,Jianlin An,Yinjun Tian
DOI: https://doi.org/10.1016/j.matchar.2024.114578
IF: 4.537
2024-12-04
Materials Characterization
Abstract:In this study, an Al-Mn-Mg-Sc-Zr alloy was prepared using the selective laser melting (SLM) technique, and the precipitation behavior during heating was characterized by In-situ transmission electronic microscopy (TEM). The results show that the microstructure of the deposited alloy is mainly composed of columnar crystals in the molten pool and equiaxed crystals at the bottom edge of the molten pool. Al 6 Mn was identified as the major phase within the deposited alloy, in which Al 6 Mn showed rod-shaped and particulate behavior distributed along the grain boundary of columnar crystal and equiaxed crystal. A detailed characterization of the precipitation behavior was conducted using in-situ TEM at various temperatures. At 250 °C, it was observed that the dislocation density decreased with heating time, showing no precipitation behavior, indicating good thermal stability of the alloy at this temperature. After the temperature was raised from 250 °C to 425 °C, a large number of fine and dispersed needle-rod secondary Al 6 Mn phases were precipitated in the inner and bottom of the molten pool. With the increase in heating time, the size of the needle-rod secondary Al 6 Mn phase increased, and no Al 3 Sc precipitates were observed. However, the precipitation of Al 3 Sc was found by ex-situ TEM. Thermodynamic properties of Al 3 Sc and Al 6 Mn were calculated by first principles. It is found that the free energy of Al 6 Mn is lower than that of Al 3 Sc in the temperature range of 85 to 800 K, which indicates that Al 3 Sc has better thermodynamic stability than Al 6 Mn.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing