Abstract:TiO2-diatomite photocatalysts were prepared by sol-gel process with various pre-modified diatomite. In order to obtain diatomite with different surface characteristics, two modification approaches including calcination and phosphoric acid treatment on the micro-structure of diatomite are introduced. The photocatalysts were characterized by XRD, XPS, nitrogen adsorption-desorption isotherms and micromorphology analysis. The results indicate that, compared with pure TiO2, the anatase-to-rutile phase transition temperature of TiO2 loaded on diatomite carrier is significantly increased to nearly 900 degrees C, depending on the different pretreatment method of diatomite. The photocatalytic activities of different samples were evaluated by their degradation rate of methyl orange ( MO) dye under UV and visible-light irradiation. The samples prepared by phosphoric acid pretreatment method exhibit the highest photocatalytic activity. After 90 min of UV irradiation, about 90% of MO is decomposed by the best effective photocatalyst. And after 8 h visible-light irradiation, nearly 60% of MO is decomposed by the same sample. Further mechanism investigation reveals that the H3PO4 pretreatment process can obviously change the surface features of diatomite carrier, cause the formation of Si-O-Ti bond, increase the binding strength between TiO2 and diatomite, restrain crystal growth of loaded TiO2, and thus form thermal-stable meso-porous structure at the granular spaces. It helps to build micro-, meso- and macro-porous hierarchical porous structure in TiO2-diatomite, and improves the charge and mass transfer efficiency during catalyzing process, resulting in the significantly increased photocatalytic activity of TiO2-diatomite pretreated by phosphoric acid. (C) 2014 Elsevier B. V. All rights reserved.

Preparation and Characterization of Highly Active Mesoporous TiO2 Photocatalysts by Hydrothermal Synthesis under Weak Acid Conditions

One-Step Synthesis Of Bifunctional Tio2 Catalysts And Their Photocatalytic Activity

Acid-regulated hydrolysis and condensation of titanium cation toward controllable synthesis of multiphase mesoporous TiO2 for effectively enhance photocatalytic H2 evolution

Self-assembly and Photocatalysis of Mesoporous TiO 2 Nanocrystal Clusters

Interface Actions Between TiO2 and Porous Diatomite on the Structure and Photocatalytic Activity of TiO2-diatomite

Preparation and Performance of Mesoporous TiO<sub>2</sub> Photocatalyst with P123 As Template

Facile Synthesis and Active Photocatalysis of Mesoporous and Microporous Tio2 Nanoparticles

Direct Sonochemical Preparation And Characterization Of Highly Active Mesoporous Tio2 With A Bicrystalline Framework

Rapid synthesis of mesoporous TiO2 with high photocatalytic activity by ultrasound-induced agglomeration

Synthesis and Characterization of Phosphated Mesoporous Titanium Dioxide with High Photocatalytic Activity

Synthesis of Well-Ordered Mesoporous Titania with Tunable Phase Content and High Photoactivity

Characterization of Mesoporous Nanocrystalline TiO2 Photocatalysts Synthesized Via a Sol-Solvothermal Process at a Low Temperature

Controllable Synthesis of Mesoporous TiO2 Polymorphs with Tunable Crystal Structure for Enhanced Photocatalytic H2 Production

Preparation and photocatalytic activity of mesoporous TiO2 derived from hydrolysis condensation with TX-100 as template

Direct Sonochemical Preparation and Characterization of Highly Active Mesoporous TiO<sub>2</sub>with a Bicrystalline Framework

Mesoporous titania with high crystallinity during synthesis by dual template system as an efficient photocatalyst

Using phosphoric acid as a catalyst to control the structures of mesoporous titanium dioxide materials

Synthesis and Characterization of Mesoporous-Tio2 with Enhanced Photocatalytic Activity for the Degradation of Chloro-Phenol

Hydrothermal Synthesis and Morphological Evolution of Mesoporous Titania−Silica

Sonochemical Synthesis and Photocatalytic Activity of Meso- and Macro-Porous TiO(2) for Oxidation of Toluene.

Synthesis of Mesoporous Titania with High Photocatalytic Activity by Nanocrystalline Particle Assembly