Effect of B-site cation nonstoichiometric ratio on the properties of 0.6BCN-0.4BZN ceramics

Lü Xin,ZHONG Chaowei,ZHANG Shuren,REN Rui

DOI: https://doi.org/10.3969/j.issn.1001-2028.2010.09.013

2010-01-01

Abstract:Ba(Co0.6Zn0.4)(1/3)Nb2/3O3(0.6BCN-0.4BZN) microwave dielectric ceramics were prepared by using the conventional solid-state method.The effects of B-site(Co,Zn) cation nonstoichometric ratio(x=-0.015,-0.009,-0.003,0,0.003,0.009,0.015) on the microwave dielectric properties of prepared Ba(Co0.6Zn0.4)(1/3+x)Nb2/3O3 ceramics were investigated.The results indicate that slight B site cation deficiency can increase the densification degree of the 0.6BCN-0.4BZN microwave dielectric ceramics.Meanwhile,the density with a maximum(above 99% of theoretical density) can be achieved while the x value is-0.009.Especially,when the ceramics are sintered at 1 400 ℃ for 20 h,the relative permittivity and the Q.f value measured at 5.180 GHz are 35.35 and 40 787 GHz,respectively.The temperature coefficient of resonant frequency(τf) shows a negative value of-3×10-6 /℃.