Abstract:The sulfide precipitation has been widely used to recover Cu(II) and remove As(V) in copper smelting electrolyte based on the Cu(II)-As(V) separation. However, the recovery efficiency was undesirable due to the inaccurate control of process parameters. It was necessary to investigate the process and mechanisms of sulfurization precipitation for accurate adjustment. Herein, under the single and mixed solutions of Cu(II) and As(V), the process parameters were investigated and the precipitation mechanisms were explored. And when using actual electrolytes, the corresponding sulfurization process and mechanisms were also revealed. The sulfurization results of single component solutions suggested that Cu(II) was rapidly precipitated in one step, but As(V) firstly generated intermediate, then it was gradually reduced to As(III) for a longer time and quickly precipitated in the form of amorphous. This phenomenon caused the significantly faster removal speed of Cu(II) than that of As(V). For their mixed solutions, only a small amount of As(V) were removed by adsorbing the precipitate at the low S/Cu molar ratios (RS/Cu), and Cu(II) and As(V) could achieve a good separation. Simultaneously, it revealed that the sulfidation competitive mechanisms were related to the solubility product constant (Ksp) and initial As(V) concentrations. In addition, the similar rules were also observed in actual electrolytes. Moreover, under RS/Cu = 1.2 and reaction time of 10 min, the arsenic content of sulfide precipitates in the actual electrolyte was less than 2.5%, which showed a great separation also could be obtained for the actual electrolyte. This result met the requirement of Cu(II) recovery. It can provide a good reference for adjusting sulfidation parameters in the actual process to achieve efficient copper recovery, reduce the production of hazardous waste containing arsenic at the source and realize the cleaner production of copper smelting system.

Research Status on Preparation Process for Copper Sulfate

Study on preparation process of sodium sulfantimonate by sodium antimonate

Study on the mechanism of copper and arsenic separation in copper smelting acidic solution by arsenic sulfide residue

Remove of Arsenic, Antimony and Bismuth from Crude Crystal Copper Sulfate

Technology of Preparation for Sponge Copper Powder by Leaching-Electrowinning from the Complex Multi-metal and Low Metal Grade Ores

The Sulfurization Precipitation and Competition Mechanisms of Cu(II) and As(V) in Electrolyte Towards Efficient Recovery of Copper

Optimization of Processes for Preparation of Cuprous Oxide by Sodium Sulfite Reduction

Cyanide-free copper electroplating in sulfite/thiosulfate bath

Study on the Copper Sulfate Crystalline Mother Liquor by Eletrodialysis Process

Reaction Behavior of Na2SO4-Containing Copper Matte Powders in a Simulated Flash Converting Process

Progress in Electroplating of Copper from Sulfate Bath

Status-in-art of Preparation and Production of Ultra-fine Copper Powder in China

Research on New Flotation Process of a Low-grade Copper Sulfide Ore in Yunnan

Mechanism study of the effect of copper ions on the stability of As(III) sulfuration precipitation in acidic copper smelting wastewater

Progress in Preparation of Ultrafine Copper Powder by Chemical Reduction Method

Experimental Study on Separation of Iron and Arsenic from Copper Sulfate Solution

Preparation of high purity tetrabasic lead sulphate

Facile Sulfurization under Ambient Condition with Na2S to Fabricate Nanostructured Copper Sulfide

Effect of Process Conditions on the Preparation of Copper Powders by Electro-Deposition

Preparation and characterization of copper powder particles

Removal of Iron During Copper Sulfate Production from Bioleaching Reextraction Solution