Morphological Evolution of Primary Β-Nb5si3 Phase in Nb-Mo-Si Alloys
Fuxin Wang,Liangshun Luo,Xianyu Meng,Yanjin Xu,Liang Wang,Yanqing Su,Jingjie Guo,Hengzhi Fu
DOI: https://doi.org/10.1016/j.jallcom.2018.01.112
IF: 6.2
2018-01-01
Journal of Alloys and Compounds
Abstract:Nb-20Si-xMo (x = 2,4,6)-based ultrahigh temperature alloys were prepared by high-vacuum non-consumable arc melting in a water-cooled copper crucible. The morphological evolution of the primary beta-Nb5Si3 phase in the Nb-Mo-Si-based alloys was discussed in detail based on the data of X-ray diffraction, field emission scanning electron microscopy and transmission electron microscopy. The results indicate that the phase constituents in the studied alloys consist of Nb solid-solution (Nbss) phase and beta-Nb5Si3 phase, with Nb3Si phases also appearing in the Nb-20Si-2Mo alloy. The Mo addition does not change the morphology of the primary beta-Nb5Si3 phase in the Nb-20Si alloy. The primary beta-Nb5Si3 phase in the investigated alloys displays various shapes, such as dendritic, L-like, hollow square and square ones. The morphological evolution of the primary beta-Nb5Si3 phase follows two main paths in the Nb-Mo-Si alloys. (I) At a lower cooling rate, the primary beta-Nb5Si3 morphology undergoes a transformation from L-like shapes to hollow square shapes before finally forming square shapes, and (II) at a higher cooling rate, the primary beta-Nb5Si3 morphology transforms from Y-like shapes to hollow square shapes and ends with forming square shapes. (C) 2018 Elsevier B.V. All rights reserved.