Microstructures and Properties of Nb–Si-based Alloys with B Addition
Liang-Shun Luo,Fu-Xin Wang,Xian-Yu Meng,Yan-Jin Xu,Liang Wang,Yan-Qing Su,Jing-Jie Guo,Heng-Zhi Fu
DOI: https://doi.org/10.1007/s12598-018-1195-7
IF: 6.318
2019-01-01
Rare Metals
Abstract:The Nb-16Si-18Ti-xB(at％,similarly here-inafter,x=0,1,2,3)alloys were prepared by arc melting in a water-cooled copper crucible.The influences of B addition on their microstructures and properties were based on the data of X-ray diffraction(XRD),field emission scanning electron microscopy(FESEM),and electronic universal material testing machine.It is found that the addition of B promotes the formation of α-Nb5Si3 phase and suppresses the formation of Nb3Si phase.B addition also tends Nb-16Si-18Ti alloy to form the hypereutectic structures.The content of silicide phases shows a trend of firstly decreasing and then increasing in Nb-16Si-18Ti-xB(x=0,1,2,3)alloys.The size of Nb solid solution(Nbss)phase increases in Nb-16Si-18Ti-xB(x=0,1,2,3)alloys after heat treatment at 1523 K for 10 h.The room temperature compression strength of Nb-16Si-18Ti alloy increases firstly and then decreases with B addition.The high-temperature compression strength of Nb-16Si-18Ti alloy decreases firstly and then increases with B addition.It is found that the volume and size of silicide phases have a synergistic effect on the compression strength of Nb-Ti-Si-based alloys.