Abstract:Joining C/C composites to Ni-based single crystal alloy DD3 can significantly broaden their industrial application. The currently used active brazing method (ABM) may cause harmful reactions with Ni-based alloys, generating brittle compounds and deteriorating joint performance. In this work, a two-step method involving chromium carbide (Cr-C) surface modification and brazing using pure Cu filler is first developed to explore avoiding brittle compounds in joints. Surprisingly, the brazed seam of joints is mainly composed of (Cu, Ni) solid solution (s, s) without generating brittle compounds. At the DD3 interface, only (Ni, Cu) (s, s) and (Cu, Ni) (s, s) layers are formed. Besides, (W, Mo) (s, s) particles are precipitated nearby the DD3 substrate. For the C/C interface, the Cu filler is tightly joined to the Cr-C layer without forming new phases. The joint microstructure has no significant change with the variation of the Cr-C layer thickness. As increased the Cr-C layer thickness, the joint strength first increases and then decreases. The maximum shear strength of ∼ 32 MPa is obtained when the Cr-C layer thickness is ∼ 4.6 μm. The joint shear strength decreases with increased testing temperatures, which can still be maintained at ∼ 28 MPa at 600 °C. The surface modification and brazing strategy in this work can be further applied to the joining of other carbon materials and ceramics with poor wettability.

The WeldabUity and Microstructure of c-BN Brazed with CuNiSnTi Filler Metal

Influence of Ni Addition on Corrosion Performance of Medium-temperature Filler Metal with Low Cu Content for Al Brazed Joints

Microstructure and properties of the C/C-superalloy brazed joint by Ni-based filler

Microstructure and mechanical properties of C/C composite joint brazed with Ni-based filler

Brazing of C/C Composite and TiAl Alloy Using TiNiSi Filler Metal Added Cu Interlayer

Microstructure and mechanical properties of cemented carbide to steel joints by electron beam welding

Interfacial microstructure and mechanical properties of WC–Co/40Cr joints brazed at low–temperature with Ag–Cu–Ti + Sn novel filler

Exploring avoiding brittle compounds in brazed joints of C/C composites and DD3 alloys through surface modification

Influence of microalloying with B on the microstructure and properties of brazed joints with Ag–Cu–Zn–Sn filler metal

Microstructural evolution and mechanical property of a SiCf/SiC composite/Ni-based superalloy joint brazed with an Au-Cu-Ti filler

Mechanical and microstructural characterization of brazing joints of the TiC/Cu–20Ni composite to Cu–20Ni

Brazing of Cr 2 AlC and 316H stainless steel using BNi-2 filler: Microstructure, properties and joining mechanism

Microstructure and Mechanical Properties of Al2O3/Cu Joints Brazed with Ag–Cu–Ti+Zn Composite Fillers

Investigating the effect of WC reinforcements in Cu Ti composite filler on the microstructural evolution and mechanical characteristics in brazing C f /SiC and GH3536

Ultra-high temperature brazing of C/C composite using pure Ni as filler based on eutectic reaction

Brazing of C/C composites and 304 stainless steels via Ni/Mo composite interlayer

Vacuum Brazing of C/C Composite and TiAl Intermetallic Alloy Using BNi-2 Brazing Filler Metal

Brazing Al2O3 to 4J42 Using Ag–Cu–Ti/Cu/BNi-2 Composite Fillers with Different Thicknesses of Cu Interlayer

Comparative analysis of the brazing mechanism and wear characteristics of brazed diamond abrasive with Zr-alloyed Cu-based filler metals

Effect of Cu-Sn-Ti solder alloy on morphology, bonding interface, and mechanical properties of cBN grits

Profiling interfacial reaction features and mechanical properties of B 4 C ceramic and Ti6Al4V titanium alloy brazed with Ag-based brazing filler