Preparation of epoxide-acrylate-polyurethane hybrid dispersions

Chen Huan-qin
2007-01-01
Abstract:The aqueous polyurethane modified by epoxide resin(WPUE) was prepared with trimethylolpropane(TMP) as cross linker, then epoxide-acrylate-polyurethane(WPUEA) hybrid dispersions were synthesized by free-radical emulsion polymerization which were carried out by using azodiisobutyronitrile (AIBN) as initiator and methyl methacrylate (MMA) as monomer.The WPUEA hybrid dispersions were characterized with FT-IR, gel permeation chromatography (GPC), Malvern particle size analyzer and TEM.The influences of the total mole ratio of NCO/OH, the type and amount of epoxide resin, the amounts of TMP and MMA on the properties of the hybrid dispersions and the coating films were studied.The experimental results showed the WPUEA hybrid emulsions had better properties at total mole ratio of-NCO/OH 1.2—1.5, TMP 4%—8%, E20 4%—6%, MMA 10%—30%.At the same time, the coating films of WPUEA showed such better properties as:hardness 0.73,gloss 85, surface drying time 30 min, freezing and thawing cycle above 5.The water resistance and solvent resistance of the films of WPUEA were improved.The modified WPUEA hybrid emulsions could substitute for solvent polyurethane.
What problem does this paper attempt to address?