Carbon Nanotube Composites Manufactured by Filament Wind Processing for Electrothermal Deicing Application
Huan Ma,Li Liu,Bangze Zhou,Xiaoxiao Wei,Wei Liu,Zhiyuan Zhang,Lamei Guo,Fujun Xu
DOI: https://doi.org/10.1021/acsanm.3c01575
IF: 6.14
2023-06-09
ACS Applied Nano Materials
Abstract:Carbon nanotube (CNT) composites are proven to be versatile tools in many fields by virtue of the multifunctional response. However, the severe challenge in mass production of CNT-based composites has become a bottleneck in both the science and engineering. To tackle the issues, herein, we reported an effective approach toward preparing densified and highly orientated CNT yarn/PVA (polyvinyl alcohol) composites via pultrusion and filament wind processing. In this processing, CNT yarn with a diameter of 150 μm, produced by twisting the CNT film directly, was dipped into PVA polymer solution and then continuously winded on a mandrel after squeezed by a pultrusion mold with a diameter of 120 μm. As a result, the pultruded CNT yarn/PVA winding composites (named as P-CNTY-WC), with the densified and aligned CNT yarn showed a considerable tensile strength (708.38 MPa). Furthermore, its toughness was 109.92 MJ m–3, much higher than those of the reported high-performance fiber reinforced composites. Additionally, the P-CNTY-WC possessed high electrical conductivity (207 S cm–1) and thus exhibited a rapid electrothermal performance (reached to 221 °C at 1.5 V within 30 s). In view of the high electrical performances, the electrothermal deicing application in the aircraft wing was demonstrated. Thereby, the facile way and attractive properties could provide insights into massive production of high-performance structural composites with multifunctional applications.
materials science, multidisciplinary,nanoscience & nanotechnology