Catalytic pyrolysis of Paulownia wood and bio-oil characterization
Derya YildizSait YorgunChemical Engineering Department,Eskişehir Osmangazi University,Eskisehir,Republic of TürkiyeDr. Derya Yıldız has been working at Eskişehir Osmangazi University,Department of Chemical Engineering since 2009. She completed her PhD at Eskişehir Osmangazi University in 2015. She is still working on renewable energy at Eskişehir Osmangazi University.Prof. Dr. Sait Yorgun has been working at Eskişehir Osmangazi University,Department of Chemical Engineering since 1994. He received his PhD degree from Istanbul Technical University in 1993. She is still working on renewable energy at Eskişehir Osmangazi University.
DOI: https://doi.org/10.1080/15567036.2023.2289563
2024-01-13
Energy Sources Part A Recovery Utilization and Environmental Effects
Abstract:This study focused on the catalytic pyrolysis of Paulownia (P. elongota) wood. The effects of ZSM-5, Na 2 CO 3 , sepiolite, and catalyst ratio (10–80% by wood weight) on product yields and bio-oil composition were investigated. In pyrolysis experiments, 500°C pyrolysis temperature, 50°C min −1 heating rate, and 100 mL min −1 N 2 flow rate were kept as constant. The catalyst type and catalyst ratio changed the product yields and bio-oil compositions. Pyrolysis conversion was increased for all catalyst types. Maximum liquid product yields were obtained as 63.26 wt%, 56.18 wt%, and 54.59 wt% with the ZSM-5, Na 2 CO 3 and sepiolite, respectively, at 10 wt% catalyst ratio. For all catalysts, it was determined that the liquid and solid yields reduce and the gas product yield rises with the catalyst ratio. The bio-oil characterization was performed with elemental analysis, FTIR, 1 HNMR, and GC-MS techniques. The bio-oil composition was determined to consist of alkanes, carboxylic acids, ketones, esters, benzenes, and phenols.
energy & fuels,engineering, chemical