Effects of Triple Heat Treatment on Stress Relaxation Resistance of Bt20 Alloy

Liu Yong,Zhu Jingchuan
DOI: https://doi.org/10.1016/j.mechmat.2008.04.004
IF: 4.137
2008-01-01
Mechanics of Materials
Abstract:The BT20 alloy was treated by triple heat treatment as follows: quenching at 1020°C with water cooling followed by aging at 750°C for 100min and aging at 550°C for 2h. And basketweave microstructure was obtained, which shows random relative orientation between α and β phase. BT20 alloy treated with “Triple heat treatment” shows higher stress relaxation resistance than that in equiaxed and widmenstaten microstructure.