Abstract:A fine-grained TiAl alloy with a composition of Ti-47%Al(mole fraction) was prepared by double mechanical milling(DMM) and spark plasma sintering(SPS). The relationship among sintering temperature, microstructure and mechanical properties of Ti-47%Al alloy was studied by X-ray diffractometry(XRD), scanning electron microscopy(SEM) and mechanical testing. The results show that the morphology of double mechanical milling powder is regular with size of 20−40 μm. The main phase TiAl and few phases Ti3Al and Ti2Al were observed in the SPS bulk samples. For samples sintered at 1000 °C, the equiaxed crystal grain was achieved with size of 100−250 nm. The samples exhibited compressive and bending properties at room temperature with compressive strength of 2013 MPa, compression ratio of 4.6% and bending strength of 896 MPa. For samples sintered at 1100 °C, the size of equiaxed crystal grain was obviously increased. The SPS bulk samples exhibited uniform microstructures, with equiaxed TiAl phase and lamellar Ti3Al phase were observed. The samples exhibited compressive and bending properties at room temperature with compressive strength of 1990 MPa, compression ratio of 6.0% and bending strength of 705 MPa. The micro-hardness of the SPS bulk samples sintered at 1000 °C is obviously higher than that of the samples sintered at 1100 °C. The compression fracture mode of the SPS TiAl alloy samples is intergranular fracture and the bending fracture mode of the SPS TiAl alloy samples is intergranular rupture and cleavage fracture.

Sintering Process via Solid-State Reaction of Ti/Al Composite Powders Prepared by High-Energy Ball Milling

Preparation of TiAl-based alloys by mechanical milling and reactive sintering

Preparation of Ti/Al based nanophase composite powder by mechanical alloying

Manufacturing a TiAl Alloy by High-Energy Ball Milling and Subsequent Reactive Sintering

Preparation of ti-al based nanophase composite powder by mechanical alloying

Densification behavior during reactive sintering of compacted Ti/Al composite powders prepared by high-energy ball milling

Microstructure and Properties of A Tial Alloy Prepared by Mechanical Milling and Subsequent Reactive Sintering

Effect of mechanical milling on diffusive reaction of Ti-Al composite powders

Expansion and Dehiscence Behaviors During Low-Temperature Reactive Sintering of Compact Ti/Al Composite Powders Prepared by High-Energy Ball Milling

Synthesis of Tial Based Alloy by Mechanical Milling, Warm Pressing and Reactive Sintering

Microstructure evolution of TiAl composite powder during low temperature high-energy milling

Synthesis and Properties of an Ultrafine Grained Ti-45al-2cr-2nb-1b-0.5ta Alloy Prepared by Double Mechanical Milling and Spark Plasma Sintering

Microstructure of TiAl alloy prepared by intense plastic deformation and subsequent reaction sintering

Investigation on nanocrystalline TiAl based powders prepared by double-steps ball milling

Fine-grained TiAl alloy prepared by double mechanical milling and spark plasma sintering

Preparation of fine-grains TiAl alloys by mechanical alloying and spark plasma sintering

Investigation on the Influence of Mechanical Milling on Microstructure and Thermostability of Ti/Al Mixed Powders

Spark Plasma Sintering Mechanisms of the Al-Zn-Mg-Cu Alloys and TiB2/Al-Zn-Mg-Cu Composites

Microstructures and Mechanical Properties of TiAl Alloy Prepared by Spark Plasma Sintering

Microstructural Characters of TiAl Intermetallics Prepared with Different Processes

EFFECTS OF HIGH-ENERGY BALL MILLING ON THE STRUCTURE AND PROPERTY OF A MULTIPHASE Al3Ti-BASED INTERMETALLIC ALLOY